Direct real-space observation of nearly stochastic behavior in magnetization reversal process on a nanoscale

Conference · Fri Jun 01 04:00:00 EDT 2007

OSTI ID:940565

Im, M -Y; Kim, D -H; Lee, K -D; Fischer, P; Shin, S -C

We report a non-deterministic nature in the magnetization reversal of nanograins of CoCrPt alloy film. Magnetization reversal process of CoCrPt alloy film is investigated using high resolution soft X-ray microscopy which provides real space images with a spatial resolution of 15 nm. Domain nucleation sites mostly appear stochastically distributed within repeated hysteretic cycles, where the correlation increases as the strength of the applied magnetic field increases in the descending and ascending branches of the major hysteresis loop. In addition, domain configuration is mostly asymmetric with inversion of an applied magnetic field in the hysteretic cycle. Nanomagnetic simulation considering thermal fluctuations of the magnetic moments of the grains explains the nearly stochastic nature of the domain nucleation behavior observed in CoCrPt alloy film. With the bit size in high-density magnetic recording media approaching nanometer length scale, one of the fundamental and crucial issues is whether the domain nucleation during magnetization reversal process exhibits a deterministic behavior. Repeatability of local domain nucleation and deterministic switching behavior are basic and essential factors for achieving high performance in high-density magnetic recording [1-3]. Most experimental studies on this issue reported so far have been mainly performed by indirect probes through macroscopic hysteresis loop and Barkhausen pattern measurements, which provide the ensemble-average magnetization. Thus, they are inadequate to gain insight into the domain-nucleation behavior on a nanometer length scale during the magnetization reversal process [4-6]. Very recently, coherent X-ray speckle metrology, where the speckle pattern observed in reciprocal space acts as a fingerprint of the domain configurations, was adopted to investigate stochastic behavior in the magnetization reversal of a Co/Pt multilayer film [7,8]. However, no direct observation on the stochastic behavior of domain nucleation during magnetization reversal in real space at the nanometer scale has yet been reported. The main reason is due to limitations of the microscopic measurement techniques employed. Thus, experimental confirmation for stochastic behavior of domain nucleation together with its clarification has to date remained a scientific challenge.

• Research Organization: Ernest Orlando Lawrence Berkeley National Laboratory, Berkeley, CA (US)
• Sponsoring Organization: Materials Sciences Division
• DOE Contract Number: AC02-05CH11231
• OSTI ID: 940565
• Report Number(s): LBNL-1145E
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ALLOYS
CONFIGURATION
FLUCTUATIONS
HYSTERESIS
MAGNETIC FIELDS
MAGNETIC MATERIALS
MAGNETIC MOMENTS
MAGNETISM
MAGNETIZATION
MICROSCOPY
NUCLEATION
PROBES
RESOLUTION
SPATIAL RESOLUTION
Stochastic nature nucleation magnetization reversal