ELECTROCHEMICAL CORROSION REPORT FOR TANKS 241-AW-103 & 241-AZ-102 & 241-AN-106 & 241-AN-107 & 241-AY-101 & 241-AY-102
Corrosion rates using supernatant samples retrieved from near the top of the liquid layer were determined for the tanks. Corrosion rates using settled solids (saltcake) were determined. The supernatant samples were tested as received without argon sparging. The settled solid sample segments were extruded under anaerobic condition and kept under a sweep of humidified argon gas during 'the electrochemical corrosion testing. The class of steel used to construct the tank in question was used, and test coupons were allowed to equilibrate for a minimum of 18 hours before a Tafel scan was initiated. The coupons were scanned from -250 mV to +250 mV from the rest or open circuit potential. The corrosion rate is reported along with the corrosion current measurement, open circuit potential, and a chi-square statistic generated by the instrument controlling and analysis algorithm.
- Research Organization:
- Hanford Site (HNF), Richland, WA
- Sponsoring Organization:
- USDOE Assistant Secretary for Environmental Management (EM)
- DOE Contract Number:
- AC27-99RL14047
- OSTI ID:
- 940017
- Report Number(s):
- RPP-RPT-34697 Rev 0
- Country of Publication:
- United States
- Language:
- English
Similar Records
ELECTROCHEMICAL CORROSION TEST RESULTS FOR TANK 241-SY-102 SUPERNATE GRAB SAMPLES
ELECTROCHEMICAL CORROSION TESTING OF TANKS 241-AN-102 & 241-AP-107 & 241-AP-108 IN SUPPORT OF ULTRASONIC TESTING
ELECTROCHEMICAL CORROSION TESTS FOR TANK 241-AY-101 CORE 325 SEGMENTS 16R1 & 16R2
Technical Report
·
Mon Apr 09 00:00:00 EDT 2007
·
OSTI ID:940014
ELECTROCHEMICAL CORROSION TESTING OF TANKS 241-AN-102 & 241-AP-107 & 241-AP-108 IN SUPPORT OF ULTRASONIC TESTING
Technical Report
·
Wed Nov 19 23:00:00 EST 2008
·
OSTI ID:943339
ELECTROCHEMICAL CORROSION TESTS FOR TANK 241-AY-101 CORE 325 SEGMENTS 16R1 & 16R2
Technical Report
·
Tue Nov 13 23:00:00 EST 2007
·
OSTI ID:940019