Effect of filler metal composition on the strength of yttria stabilized zirconia joints brazed with Pd-Ag-CuOx
Journal Article
·
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, 39(9):2095-2105
The Ag-CuOx system is of interest to be used to be used as an air braze filler metal for joining high temperature electrochemical devices. Previous work has shown that the melting temperatures can be increased by adding palladium to Ag-CuOx and it is expected that this may aid high temperature stability. This work compares the room temperature bend strength of joints made between yttria-stabilized zirconia (YSZ) air brazed using Ag-CuOx without palladium and with 5 and 15mol% palladium additions. It has been found that in general palladium decreases joint strength, especially in low copper oxide compositions filler metals. At high copper oxide contents, brittle fracture through both copper oxide rich phases and the YSZ limits joint strength.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (US)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 939009
- Report Number(s):
- PNNL-SA-56438; AA1510100
- Journal Information:
- Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, 39(9):2095-2105, Journal Name: Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, 39(9):2095-2105 Journal Issue: 9 Vol. 39; ISSN 1073-5623; ISSN MMTAEB
- Country of Publication:
- United States
- Language:
- English
Similar Records
High Temperature Strength of YSZ Joints Brazed with Palladium Silver Copper Oxide Filler Metals
JOINING OF ADVANCED HIGH-TEMPERATURE MATERIALS
Investigation of Pd-Modified Ag-CuO Air Braze Filler Metals
Journal Article
·
Wed Jun 09 00:00:00 EDT 2010
· International Journal of Hydrogen Energy, 36(7):4519-4524
·
OSTI ID:1019218
JOINING OF ADVANCED HIGH-TEMPERATURE MATERIALS
Conference
·
Thu May 14 00:00:00 EDT 2009
·
OSTI ID:1240236
Investigation of Pd-Modified Ag-CuO Air Braze Filler Metals
Conference
·
Sat Dec 31 23:00:00 EST 2005
·
OSTI ID:948425