CHARACTERIZATION OF VITRIFIED SAVANNAH RIVER SITE SB4 WASTE SURROGATE PRODUCED IN COLD CRUCIBLE

Conference · Tue Aug 05 04:00:00 EDT 2008

OSTI ID:935778

Marra, J

Savannah River Site (SRS) sludge batch 4 (SB4) waste surrogate with high aluminum and iron content was vitrified with commercially available Frit 503-R4 (8 wt.% Li{sub 2}O, 16 wt.% B2O3, 76 wt.% SiO{sub 2}) by cold crucible inductive melting using lab- (56 mm inner diameter), bench- (236 mm) and large-scale (418 mm) cold crucible. The waste loading ranged between 40 and 60 wt.%. The vitrified products obtained in the lab-scale cold crucible were nearly amorphous with traces of unreacted quartz in the product with 40 wt.% waste loading and traces of spinel phase in the product with 50 wt.% waste loading. The glassy products obtained in the bench-scale cold crucible are composed of major vitreous and minor iron-rich spinel phase whose content at {approx}60 wt.% waste loading may achieve {approx}10 vol.%. The vitrified waste obtained in the large-scale cold crucible was also composed of major vitreous and minor spinel structure phases. No nepheline phase has been found. Average degree of crystallinity was estimated to be {approx}12 vol.%. Anionic motif of the glass network is built from rather short metasilicate chains and boron-oxygen constituent based on boron-oxygen triangular units.

• Research Organization: SRS
• Sponsoring Organization: DOE
• DOE Contract Number: AC09-08SR22470
• OSTI ID: 935778
• Report Number(s): SRNS-STI-2008-00018
• Country of Publication: United States
• Language: English

Related Subjects

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE WASTES FROM NUCLEAR FACILITIES
36 MATERIALS SCIENCE
GLASS
PHASE STUDIES
RADIOACTIVE WASTE PROCESSING
SLUDGES
SPINELS
VITRIFICATION
WASTE FORMS