Effects of Impurities on Alumina-Niobium InterfacialMicrostructures
Optical microscopy, scanning electron microscopy, and transmission electron microscopy were employed to examine the interfacial microstructural effects of impurities in alumina substrates used to fabricate alumina-niobium interfaces via liquid-film-assisted joining. Three types of alumina were used: undoped high-purity single-crystal sapphire; a high-purity, high-strength polycrystalline alumina; and a lower-purity, lower-strength polycrystalline alumina. Interfaces formed between niobium and both the sapphire and high-purity polycrystalline alumina were free of detectable levels of impurities. In the lower-purity alumina, niobium silicides were observed at the alumina-niobium interface and on alumina grain boundaries near the interface. These silicides formed in small-grained regions of the alumina and were found to grow from the interface into the alumina along grain boundaries. Smaller silicide precipitates found on grain boundaries are believed to form upon cooling from the bonding temperature.
- Research Organization:
- Ernest Orlando Lawrence Berkeley NationalLaboratory, Berkeley, CA (US)
- Sponsoring Organization:
- USDOE Director. Office of Science. Basic EnergySciences
- DOE Contract Number:
- AC02-05CH11231
- OSTI ID:
- 919917
- Report Number(s):
- LBNL--57155; BnR: KC0201020
- Journal Information:
- Materials Characterization, Journal Name: Materials Characterization Journal Issue: 1 Vol. 57; ISSN 1044-5803; ISSN MACHEX
- Country of Publication:
- United States
- Language:
- English
Similar Records
Liquid-film assisted formation of alumina/niobium interfaces
The influence of interface impurities on fracture energy of UHV diffusion bonded metal-ceramic bicrystals