Measurements of photocathode operational lifetime at beam currents up to 10-mA using an improved DC high voltage GaAs photogun
Conference
·
OSTI ID:917249
This work extends past research at Jefferson Lab aimed at better appreciating the mechanisms that limit photocathode operational lifetime at high current (> 1 mA). Specifically, the performance of an improved 100 kV DC high voltage load locked photogun will be described. Although difficult to measure directly, we believe the new gun has better vacuum conditions compared to the original gun, as indicated by enhanced photocathode lifetimes exceeding 2000 C using a 1.55 mm diameter drive laser spot at the photocathode. In addition, the dependence of the lifetime on the laser spot size at the photocathode was measured and a charge density lifetime exceeding 10^6 C/cm^2 was measured with a 0.32 mm laser spot diameter.
- Research Organization:
- Thomas Jefferson National Accelerator Facility, Newport News, VA
- Sponsoring Organization:
- USDOE - Office of Energy Research (ER)
- DOE Contract Number:
- AC05-06OR23177
- OSTI ID:
- 917249
- Report Number(s):
- JLAB-ACC-06-589; DOE/OR/23177-0157
- Country of Publication:
- United States
- Language:
- English
Similar Records
Measurements of Photocathode Operational Lifetime at Beam Currents up to 10 mA using an Improved DC High Voltage GaAs Photogun
DEVELOPMENT OF A 300 KV DC HIGH VOLTAGE PHOTOGUN AND BEAM BASED STUDIES OF ALKALI NTIMONIDE PHOTOCATHODES
DC photogun vacuum characterization through photocathode lifetime studies
Journal Article
·
Wed Jun 13 00:00:00 EDT 2007
· AIP Conference Proceedings
·
OSTI ID:21061854
DEVELOPMENT OF A 300 KV DC HIGH VOLTAGE PHOTOGUN AND BEAM BASED STUDIES OF ALKALI NTIMONIDE PHOTOCATHODES
Thesis/Dissertation
·
Fri Nov 30 23:00:00 EST 2018
·
OSTI ID:1924638
DC photogun vacuum characterization through photocathode lifetime studies
Conference
·
Mon Jul 02 00:00:00 EDT 2007
·
OSTI ID:917021