Phases in ceria-zirconia binary oxide (1-x)CeO2-xZrO2 nanoparticles: the size effects
The phases of ceria-zirconia nanoparticles observed in air are studied as a function of particle size and composition by X-ray diffraction, transmission electron microscopy, and Raman spectroscopy. The emergence of two tetragonal phases t{prime}{prime} and t monotonically moves toward higher zirconia concentrations with decreasing particle size. A smaller particle size increases the solubility of zirconia in cubic ceria, while higher zirconia content in ceria stabilizes against coarsening. In particular, the cubic Ce{sub 1-x}Zr{sub x}O{sub 2-y} is persistent and is 8% in phase amount even at 90% zirconia with 33 nm crystal size. Neither the monoclinic phase m nor the tetragonal phase t{prime} is observed in the present nanoparticles (<40 nm). The effectiveness of these nanoparticles as oxygen source-and-sink in catalytic support is largely due to the persistence of the cubic and the t{prime}{prime} phases.
- Research Organization:
- Brookhaven National Laboratory (BNL) National Synchrotron Light Source
- Sponsoring Organization:
- Doe - Office Of Science
- DOE Contract Number:
- AC02-98CH10886
- OSTI ID:
- 914064
- Report Number(s):
- BNL--78632-2007-JA
- Journal Information:
- J. Am. Ceram. Soc., Journal Name: J. Am. Ceram. Soc. Journal Issue: 3 Vol. 80; ISSN 0002-7820; ISSN JACTAW
- Country of Publication:
- United States
- Language:
- English
Similar Records
Zirconia-ceria solid solution synthesis and the temperature-time-transformation diagram for the 1:1 composition
TEM observation of reaction at the interface between yttria-doped ceria and yttria-stabilized zirconia