NEUTRON-INDUCED SWELLING OF Fe-Cr BINARY ALLOYS IN FFTF AT ~400 DEGREES C
Book
·
OSTI ID:902422
The purpose of this effort is to determine the influence of dpa rate, He/dpa ratio and composition on the void swelling of simple binary Fe-Cr alloys. Contrary to the behavior of swelling of model fcc Fe-Cr-Ni alloys irradiated in the same FFTF-MOTA experiment, model bcc Fe-Cr alloys do not exhibit a dependence of swelling on dpa rate at approximately 400 degrees C. This is surprising in that an apparent flux-sensitivity was observed in an earlier comparative irradiation of Fe-Cr binaries conducted in EBR-II and FFTF. The difference in behavior is ascribed to the higher helium generation rates of Fe-Cr alloys in EBR-II compared to that of FFTF, and also the fact that lower dpa rates in FFTF are accompanied by progressively lower helium generation rates.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (US)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 902422
- Report Number(s):
- PNNL-SA-38242; AT6020100
- Country of Publication:
- United States
- Language:
- English
Similar Records
INFLUENCE OF CARBON AND DPA RATE ON NEUTRON-INDUCED SWELLING OF Fe-15Cr-16Ni-0.25Ti IN FFTF AT ~400 DEGREES C
Influence of Composition, Helium Generation Rate and Dpa Rate on Neutron-Induced Swelling of Fe-15Cr-16Ni-0.25Ti Alloys in FFTF at {approx} 400 Degrees C
Void swelling in binary Fe-Cr alloys at 200 dpa
Book
·
Mon Dec 30 23:00:00 EST 2002
·
OSTI ID:902424
Influence of Composition, Helium Generation Rate and Dpa Rate on Neutron-Induced Swelling of Fe-15Cr-16Ni-0.25Ti Alloys in FFTF at {approx} 400 Degrees C
Conference
·
Tue Aug 05 00:00:00 EDT 2003
·
OSTI ID:15007889
Void swelling in binary Fe-Cr alloys at 200 dpa
Technical Report
·
Thu Sep 01 00:00:00 EDT 1994
·
OSTI ID:47736