OVERAGING OF OUTOKUMPU CuCrZr AT 600 DEGREES C
Book
·
OSTI ID:902060
An attempt is being made to alter the starting microstructure of CuCrZr to produce a microstructure that is not as sensitive to overageing under irradiation as the prime aged condition. Different overageing conditions (600, 700 and 800 degrees C for 4 hours) have been examined in an earlier report, and in this report shorter overageing times at 600 degrees C have been examined. Overageing times of 1 and 2 hours resulted in a microstructure that is similar in overall precipitate size and density to that of the oxide dispersion in GlidCop Al25. These samples will be included in future irradiation experiments to examine the effects of irradiation on the mechanical and physical properties.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (US)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 902060
- Report Number(s):
- PNNL-SA-31912; AT6020100
- Country of Publication:
- United States
- Language:
- English
Similar Records
OVERAGING OF OUTOKUMPU CuCrZr
THE EFFECT OF POST-IRRADATION ANNEALING ON STACKING FAULT TETRAHEDRA IN NEUTRON-IRRADIATED OFHC COPPER
Stress corrosion cracking of welded Alloy 600 penetration mockups
Book
·
Sat Mar 31 23:00:00 EST 2001
·
OSTI ID:984263
THE EFFECT OF POST-IRRADATION ANNEALING ON STACKING FAULT TETRAHEDRA IN NEUTRON-IRRADIATED OFHC COPPER
Book
·
Wed Sep 03 00:00:00 EDT 2003
·
OSTI ID:903273
Stress corrosion cracking of welded Alloy 600 penetration mockups
Book
·
Sat Dec 30 23:00:00 EST 1995
·
OSTI ID:203791