Investigation of a ceramic matrix composite under strain controlled fatigue condition
Book
·
OSTI ID:89759
- Air Force Inst. of Tech., Wright-Patterson Air Force Base, OH (United States). Dept. of Aeronautics and Astronautics
The fatigue behavior along with damage mechanisms and failure modes of a fiber reinforced ceramic matrix composite with a cross-ply lay-up was investigated under strain controlled mode. Two fatigue conditions involving tension-tension and tension-compression cycling were employed. The strain range versus fatigue life curves for both fatigue conditions were in agreement with each other. However, damage mechanisms and failure modes were different for both cases.
- OSTI ID:
- 89759
- Report Number(s):
- CONF-9409291-; ISBN 1-56676-220-0; TRN: IM9536%%189
- Resource Relation:
- Conference: 9. technical conference of the American Society for Composites, Newark, DE (United States), 20-22 Sep 1994; Other Information: PBD: 1994; Related Information: Is Part Of Proceedings of the American Society for Composites: Ninth technical conference; PB: 1319 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Behavior of a centrally notched cross-ply and unidirectional ceramic matrix composite in tension-compression fatigue. Master's thesis
Fatigue behavior of a cross-ply metal matrix composite at elevated temperature under the strain controlled mode
Fatigue behavior of a cross-ply metal matrix composite at elevated temperature under strain controlled mode. Master`s thesis
Technical Report
·
Tue Dec 01 00:00:00 EST 1992
·
OSTI ID:89759
Fatigue behavior of a cross-ply metal matrix composite at elevated temperature under the strain controlled mode
Journal Article
·
Wed Oct 01 00:00:00 EDT 1997
· Journal of Engineering Materials and Technology
·
OSTI ID:89759
Fatigue behavior of a cross-ply metal matrix composite at elevated temperature under strain controlled mode. Master`s thesis
Thesis/Dissertation
·
Thu Dec 01 00:00:00 EST 1994
·
OSTI ID:89759