The Nb{sub 3}Sn strand chosen for the next step in the magnet R&D of the U.S. LHC Accelerator Research Program is the 54/61 sub-element Restacked Rod Process by Oxford Instruments, Superconducting Technology. To ensure that the 0.7 mm RRP strands to be used in the upcoming LARP magnets are suitable, extensive studies were performed. Measurements included the critical current, {sub e}, using the voltage-current (V-I) method, the stability current, I{sub S}, as the minimal quench current obtained with the voltage-field (V-H) method, and RRR. Magnetization was measured at low and high fields to determine the effective filament size and to detect flux jumps. Effects of heat treatment temperature and durations on I{sub e} and I{sub S} were also studied. Using strand billet qualification and tests of strands extracted from cables, the short sample limits of magnet performance were obtained. The details and the results of this investigation are herein described.
- Research Organization:
- Fermi National Accelerator Lab. (FNAL), Batavia, IL (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC02-07CH11359
- OSTI ID:
- 897575
- Report Number(s):
- FERMILAB-PUB-06-299-TD; TRN: US0701453
- Journal Information:
- IEEE Trans.Appl.Supercond.17:2607-2610,2007, Conference: Presented at Applied Superconductivity Conference (ASC 2006), Seattle, Washington, 27 Aug - 1 Sep 2006
- Country of Publication:
- United States
- Language:
- English
Similar Records
Round and Extracted Nb3Sn Strand Tests for LARP Magnet R&D
Fabrication and test of 4m long Nb3Sn quadrupole coil made of RRP-114-127 strand