Tunneling corrosion mechanism of 25% chromium-20% nickel-niobium stainless steel in highly oxidizing nitric acid
- Sumitomo Metal Industries Ltd., Amagasaki (Japan). Research and Development Center
- Sumitomo Chemical Co. Ltd., Niihama (Japan)
Austenitic stainless steel (SS) is used commonly in chemical plants dealing with nitric acid (HNO{sub 3}) because of its high corrosion resistance. However, even SS tends to corrode intergranularly in highly oxidizing HNO{sub 3} containing oxidizing chromium or cerium ions, such as Cr{sup 6+} or Ce{sup 4+}. Furthermore, pitting corrosion, so-called tunneling corrosion or end-grain attack, occurs on the forgings in highly oxidizing HNO{sub 3}. The mechanism of tunneling corrosion and its countermeasures for a 25% Cr-20% Ni-Nb steel (UNS S31040) in a mock reprocessing plant were studied. Results indicated tunneling corrosion was a type of pitting corrosion with general and intergranular attack on pit surfaces. It propagated along metal flows with penetrations up to 2 mm in diameter and 6 mm in depth. Rates of tunneling corrosion were 3 to 13 times faster than general corrosion. Tunneling corrosion initiated and propagated parallel to metal flows on the local parts where chromium content was depleted. This method of corrosion was caused both by preferential corrosion of a low-chromium part and corrosion accelerated by the galvanic action between a low-chromium part as an anode and a high-chromium part as a cathode. The electroslag remelting process completely resolved this problem by making ingots free from continuous chromium segregation.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 89613
- Journal Information:
- Corrosion, Journal Name: Corrosion Journal Issue: 7 Vol. 51; ISSN 0010-9312; ISSN CORRAK
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corrosion of 304 stainless steel exposed to nitric acid-chloride environments
Effects of cold work, sensitization treatment, and the combination on corrosion behavior of stainless steels in nitric acid
Status of electroslag processing for production of large rotor forgings. Final report
Book
·
Fri Aug 01 00:00:00 EDT 1997
·
OSTI ID:504793
Effects of cold work, sensitization treatment, and the combination on corrosion behavior of stainless steels in nitric acid
Journal Article
·
Tue Mar 31 23:00:00 EST 1998
· Corrosion
·
OSTI ID:644350
Status of electroslag processing for production of large rotor forgings. Final report
Technical Report
·
Sat Jul 01 00:00:00 EDT 1978
·
OSTI ID:6640700