Observations of Ferrite/Austenite Transformations in the Heat Affected Zone of 2205 Duplex Stainless Steel Spot Welds Using Time Resolved X-Ray Diffraction
Time Resolved X-Ray Diffraction (TRXRD) measurements are made in the Heat Affected Zone (HAZ) of 2205 Duplex Stainless Steel (DSS) spot welds. Both the {gamma} {yields} {delta} and {delta} {yields} {gamma} transformations are monitored as a function of time during the rapid spot weld heating and cooling cycles. These observations are then correlated with calculated thermal cycles. Where the peak temperatures are highest ({approx}1342 C), the {gamma} {yields} {delta} transformation proceeds to completion, leaving a ferritic microstructure at the end of heating. With lower peak temperatures, the {gamma} {yields} {delta} transformation proceeds to only partial completion, resulting in a microstructure containing both transformed and untransformed austenite. Further analyses of the individual diffraction patterns show shifts in the peak positions and peak widths as a function of both time and temperature. In addition, these changes in the peak characteristics are correlated with measured changes in the ferrite volume fraction. Such changes in the peak positions and widths during the {gamma} {yields} {delta} transformation provide an indication of changes occurring in each phase. These changes in peak properties can be correlated with the diffusion of nitrogen and other substitutional alloying elements, which are recognized as the primary mechanisms for this transformation. Upon cooling, the {delta} {yields} {gamma} transformation is observed to proceed from both the completely and partially transformed microstructural regions in the TRXRD data. An examination of the resulting microstructures confirms the TRXRD observation as the evidence shows that austenite both nucleates and grows from the ferritic microstructure at locations closest to the fusion zone boundary and grows from untransformed austenite grains at locations further from this boundary.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 891387
- Report Number(s):
- UCRL-JRNL-201248; TRN: US200621%%907
- Journal Information:
- Materials Science and Engineering A, vol. 374, no. 1-2, June 1, 2004, pp. 307-321, Journal Name: Materials Science and Engineering A, vol. 374, no. 1-2, June 1, 2004, pp. 307-321
- Country of Publication:
- United States
- Language:
- English
Similar Records
In-Situ Observations of Phase Transformations in the HAZ of 2205 Duplex Stainless Steel Weldments
Investigation of the Kinetics of the Ferrite/Austenite Phase Transformation in the HAZ of a 2205 Duplex Stainless Steel Weldment