Corrosion Behavior of Alloy 22 in Chloride Solutions Containing Organic Acids
Conference
·
OSTI ID:881895
Alloy 22 (N06022) is a nickel based alloy containing alloying elements such as chromium, molybdenum and tungsten. It is highly corrosion resistant both under reducing and under oxidizing conditions. Electrochemical studies such as electrochemical impedance spectroscopy (EIS) were performed to determine the corrosion behavior of Alloy 22 in 1M NaCl solutions at various pH values from acidic to neutral at 90 C. Tests were also carried out in NaCl solutions containing oxalic acid or acetic acid. It is shown that the corrosion rate of Alloy 22 was higher in a solution containing oxalic acid than in a solution of the same pH acidified with HCl. Acetic acid was not corrosive to Alloy 22. The corrosivity of oxalic acid was attributed to its capacity to form stable complex species with metallic cations from Alloy 22.
- Research Organization:
- Lawrence Livermore National Laboratory (LLNL), Livermore, CA
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 881895
- Report Number(s):
- UCRL-CONF-216907
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Organic Acid Additions on the General and Localized Corrosion Susceptibility of Alloy 22 in Chloride Solutions
Passivity of Alloy 22 in Chloride and Fluoride Containing Solutions
Corrosion Behavior of Alloy 22 in Oxalic Acid and Sodium Chloride Solutions
Conference
·
Tue Aug 28 00:00:00 EDT 2007
·
OSTI ID:924963
Passivity of Alloy 22 in Chloride and Fluoride Containing Solutions
Conference
·
Tue Jun 07 00:00:00 EDT 2005
·
OSTI ID:881069
Corrosion Behavior of Alloy 22 in Oxalic Acid and Sodium Chloride Solutions
Conference
·
Tue Jun 24 00:00:00 EDT 2003
·
OSTI ID:15007541