Preferentially oriented, High temperature superconductors by seeding and a method for their preparation
- Knoxville, TN
A multi-domained bulk REBa.sub.2 Cu.sub.3 O.sub.x with low-angle domain boundaries which resembles a quasi-single domained material and a method for producing the same comprising arranging multiple seeds, which can be small single crystals, single domained melt-textured REBa.sub.2 Cu.sub.3 O.sub.x pieces, textured substrates comprised of grains with low misorientation angles, or thick film REBa.sub.2 Cu.sub.3 O.sub.x deposited on such textured substrate, such seeds being tailored for various REBa.sub.2 Cu.sub.3 O.sub.x compounds, in specific pattern and relative seed orientations on a superconductor precursor material which may be placed in contact with a porous substrate so as to reduce the amount of liquid phase in the melt. Because seeds can be arranged in virtually any pattern, high quality REBa.sub.2 Cu.sub.3 O.sub.x elements of virtually unlimited size and complex geometry can be fabricated.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- AC05-96OR22464
- Assignee:
- UT-Battelle, LLC (Oak Ridge, TN)
- Patent Number(s):
- US 6256521
- OSTI ID:
- 873830
- Country of Publication:
- United States
- Language:
- English
Similar Records
Large single domain 123 material produced by seeding with single crystal rare earth barium copper oxide single crystals
Nucleation and growth of single- and multiple-domain YBa{sub 2}Cu{sub 3}O{sub x} levitators: Influence of seed crystallography
Related Subjects
oriented
temperature
superconductors
seeding
method
preparation
multi-domained
bulk
reba
cu
low-angle
domain
boundaries
resembles
quasi-single
domained
material
producing
comprising
arranging
multiple
seeds
single
crystals
melt-textured
pieces
textured
substrates
comprised
grains
misorientation
angles
thick
film
deposited
substrate
tailored
various
compounds
specific
pattern
relative
seed
orientations
superconductor
precursor
placed
contact
porous
reduce
amount
liquid
phase
melt
arranged
virtually
quality
elements
unlimited
size
complex
geometry
fabricated
temperature superconductors
textured substrates
superconductor precursor
thick film
temperature superconductor
liquid phase
single crystal
single crystals
porous substrate
precursor material
single domain
textured substrate
complex geometry
preferentially oriented
domain boundaries
/505/