Synthesis of highly phase pure BSCCO superconductors
Patent
·
OSTI ID:870166
- La Grange Park, IL
- Glen Ellyn, IL
- Harrisville, PA
- Woodridge, IL
- Naperville, IL
An article and method of manufacture of (Bi, Pb)-Sr-Ca-Cu-O superconductor. The superconductor is manufactured by preparing a first powdered mixture of bismuth oxide, lead oxide, strontium carbonate, calcium carbonate and copper oxide. A second powdered mixture is then prepared of strontium carbonate, calcium carbonate and copper oxide. The mixtures are calcined separately with the two mixtures then combined. The resulting combined mixture is then subjected to a powder in tube deformation and thermal processing to produce a substantially phase pure (Bi, Pb)-Sr-Ca-Cu-O superconductor.
- Research Organization:
- Argonne National Laboratory (ANL), Argonne, IL (United States)
- DOE Contract Number:
- W-31109-ENG-38
- Assignee:
- University of Chicago (Chicago, IL)
- Patent Number(s):
- US 5468566
- OSTI ID:
- 870166
- Country of Publication:
- United States
- Language:
- English
The fabrication of high critical current capability bismuth superconductor tape
|
journal | May 1992 |
An alternate preparation for (Bi, Pb)2Ca2Sr2Cu3Oz
|
journal | May 1991 |
Similar Records
Synthesis of highly phase pure BSCCO superconductors
Synthesis of highly phase pure (Bi, Pb)-Sr-Ca-Cu-O superconductor
Synthesis of highly phase pure (Bi, Pb)-Sr-Ca-Cu-O superconductor
Patent
·
Tue Nov 21 00:00:00 EST 1995
·
OSTI ID:870166
+2 more
Synthesis of highly phase pure (Bi, Pb)-Sr-Ca-Cu-O superconductor
Patent
·
Sat Jan 01 00:00:00 EST 1994
·
OSTI ID:870166
+2 more
Synthesis of highly phase pure (Bi, Pb)-Sr-Ca-Cu-O superconductor
Patent
·
Tue Oct 11 00:00:00 EDT 1994
·
OSTI ID:870166
+2 more
Related Subjects
synthesis
highly
phase
pure
bscco
superconductors
article
method
manufacture
pb
-sr-ca-cu-o
superconductor
manufactured
preparing
powdered
mixture
bismuth
oxide
lead
strontium
carbonate
calcium
copper
prepared
mixtures
calcined
separately
combined
resulting
subjected
powder
tube
deformation
thermal
processing
produce
substantially
-sr-ca-cu-o superconductor
copper oxide
calcium carbonate
lead oxide
thermal processing
resulting combined
combined mixture
strontium carbonate
phase pure
powdered mixture
highly phase
bismuth oxide
/428/505/
highly
phase
pure
bscco
superconductors
article
method
manufacture
pb
-sr-ca-cu-o
superconductor
manufactured
preparing
powdered
mixture
bismuth
oxide
lead
strontium
carbonate
calcium
copper
prepared
mixtures
calcined
separately
combined
resulting
subjected
powder
tube
deformation
thermal
processing
produce
substantially
-sr-ca-cu-o superconductor
copper oxide
calcium carbonate
lead oxide
thermal processing
resulting combined
combined mixture
strontium carbonate
phase pure
powdered mixture
highly phase
bismuth oxide
/428/505/