Sealed glass coating of high temperature ceramic superconductors
Patent
·
OSTI ID:869863
- Tainan, TW
- Garnerville, NY
- Downers Grove, IL
- Darien, IL
A method and article of manufacture of a lead oxide based glass coating on a high temperature superconductor. The method includes preparing a dispersion of glass powders in a solution, applying the dispersion to the superconductor, drying the dispersion before applying another coating and heating the glass powder dispersion at temperatures below oxygen diffusion onset and above the glass melting point to form a continuous glass coating on the superconductor to establish compressive stresses which enhance the fracture strength of the superconductor.
- Research Organization:
- Argonne National Laboratory (ANL), Argonne, IL (United States)
- DOE Contract Number:
- W-31109-ENG-38
- Assignee:
- University of Chicago (Chicago, IL)
- Patent Number(s):
- US 5411938
- OSTI ID:
- 869863
- Country of Publication:
- United States
- Language:
- English
Reduced water degradation of YBaCuO by Si3N4 protective coating
|
journal | August 1990 |
Disruption, segregation, and passivation for Pd and noble-metal overlayers on Y
|
journal | July 1988 |
Environmental reactivity characteristics of copper‐oxide superconductors
|
journal | July 1993 |
Thermosetting epoxy as a moisture-resistant coating for YBa2Cu3O7
|
journal | June 1990 |
Diamondlike carbon films as protective coatings for superconducting YBa 2 Cu 3 O 7 films
|
journal | August 1993 |
Similar Records
Sealed glass coating of high temperature ceramic superconductors
Stability Considerations Using a Microscopic Stability Model Applied to a 2G Thin Film Coated Superconductor
High-temperature tensile behavior of a boron nitride-coated silicon carbide-fiber glass-ceramic composite
Patent
·
Tue May 02 00:00:00 EDT 1995
·
OSTI ID:869863
+1 more
Stability Considerations Using a Microscopic Stability Model Applied to a 2G Thin Film Coated Superconductor
Journal Article
·
Sun Apr 15 00:00:00 EDT 2018
· Journal of Superconductivity and Novel Magnetism
·
OSTI ID:869863
High-temperature tensile behavior of a boron nitride-coated silicon carbide-fiber glass-ceramic composite
Journal Article
·
Sat Jun 01 00:00:00 EDT 1996
· Journal of the American Ceramic Society
·
OSTI ID:869863
Related Subjects
sealed
glass
coating
temperature
ceramic
superconductors
method
article
manufacture
lead
oxide
based
superconductor
preparing
dispersion
powders
solution
applying
drying
heating
powder
temperatures
below
oxygen
diffusion
onset
melting
form
continuous
establish
compressive
stresses
enhance
fracture
strength
ceramic superconductor
glass coating
temperatures below
temperature superconductor
glass melt
lead oxide
temperature ceramic
compressive stress
sealed glass
ceramic superconductors
compressive stresses
oxygen diffusion
fracture strength
glass melting
glass powder
ceramic superco
/505/427/
glass
coating
temperature
ceramic
superconductors
method
article
manufacture
lead
oxide
based
superconductor
preparing
dispersion
powders
solution
applying
drying
heating
powder
temperatures
below
oxygen
diffusion
onset
melting
form
continuous
establish
compressive
stresses
enhance
fracture
strength
ceramic superconductor
glass coating
temperatures below
temperature superconductor
glass melt
lead oxide
temperature ceramic
compressive stress
sealed glass
ceramic superconductors
compressive stresses
oxygen diffusion
fracture strength
glass melting
glass powder
ceramic superco
/505/427/