Phosphate-bonded calcium aluminate cements
Patent
·
OSTI ID:868928
- Mastic Beach, NY
A method is described for making a rapid-setting phosphate-bonded cementitious material. A powdered aluminous cement is mixed with an aqueous solution of ammonium phosphate. The mixture is allowed to set to form an amorphous cementitious material which also may be hydrothermally treated at a temperature of from about 120.degree. C. to about 300.degree. C. to form a crystal-containing phosphate-bonded material. Also described are the cementitious products of this method and the cement composition which includes aluminous cement and ammonium polyphosphate.
- Research Organization:
- Associated Universities, Inc., Upton, NY (United States)
- DOE Contract Number:
- AC02-76CH00016
- Assignee:
- Associated Universities, Inc. (Washington, DC)
- Patent Number(s):
- US 5246496
- OSTI ID:
- 868928
- Country of Publication:
- United States
- Language:
- English
Strength Development in Phosphate-Bonded Calcium Aluminate Cements
|
journal | May 1991 |
Studies of strength mechanism in newly developed chemically bonded ceramics in the system CaOSiO2P2O5H2O
|
journal | January 1988 |
Investigation of hydration phases in the system CaO–SiO 2 -P 2 O 5 -H 2 O
|
journal | August 1988 |
Hydrothermal Preparation of Calcium Hydroxyapatite Powders
|
journal | June 1990 |
Similar Records
Phosphate-bonded calcium aluminate cements
Carbonation of calcium phosphate cements after long-term exposure to Na[sub 2]CO[sub 3]-laden water at 250[degree]C
CITRIC ACID AS A SET RETARDER FOR CALCIUM ALUMINATE PHOSPHATE CEMENTS.
Patent
·
Tue Sep 21 00:00:00 EDT 1993
·
OSTI ID:868928
Carbonation of calcium phosphate cements after long-term exposure to Na[sub 2]CO[sub 3]-laden water at 250[degree]C
Journal Article
·
Mon Nov 01 00:00:00 EST 1993
· Cement and Concrete Research; (United States)
·
OSTI ID:868928
CITRIC ACID AS A SET RETARDER FOR CALCIUM ALUMINATE PHOSPHATE CEMENTS.
Technical Report
·
Sat Jan 01 00:00:00 EST 2005
·
OSTI ID:868928
Related Subjects
phosphate-bonded
calcium
aluminate
cements
method
described
rapid-setting
cementitious
material
powdered
aluminous
cement
mixed
aqueous
solution
ammonium
phosphate
mixture
allowed
set
form
amorphous
hydrothermally
treated
temperature
120
degree
300
crystal-containing
products
composition
polyphosphate
cementitious material
cement composition
aqueous solution
ammonium phosphate
hydrothermally treated
thermally treated
calcium aluminate
/106/
calcium
aluminate
cements
method
described
rapid-setting
cementitious
material
powdered
aluminous
cement
mixed
aqueous
solution
ammonium
phosphate
mixture
allowed
set
form
amorphous
hydrothermally
treated
temperature
120
degree
300
crystal-containing
products
composition
polyphosphate
cementitious material
cement composition
aqueous solution
ammonium phosphate
hydrothermally treated
thermally treated
calcium aluminate
/106/