High temperature creep resistant austenitic alloy

Patent · Sun Jan 01 00:00:00 EST 1989

OSTI ID:867041

Maziasz, Philip J ^[1]; Swindeman, Robert W ^[1]; Goodwin, Gene M ^[2]

---

1. Oak Ridge, TN
2. Lenoir City, TN

An improved austenitic alloy having in wt % 19-21 Cr, 30-35 Ni, 1.5-2.5 Mn, 2-3 Mo, 0.1-0.4 Si, 0.3-0.5 Ti, 0.1-0.3 Nb, 0.1-0.5 V, 0.001-0.005 P, 0.08-0.12 C, 0.01-0.03 N, 0.005-0.01 B and the balance iron that is further improved by annealing for up to 1 hour at 1150.degree.-1200.degree. C. and then cold deforming 5-15 %. The alloy exhibits dramatically improved creep rupture resistance and ductility at 700.degree. C.

• Research Organization: Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
• DOE Contract Number: AC05-84OR21400
• Assignee: United States of America as represented by United States (Washington, DC)
• Patent Number(s): US 4849169
• OSTI ID: 867041
• Country of Publication: United States
• Language: English

Related Subjects

temperature
creep
resistant
austenitic
alloy
improved
wt
19-21
30-35
5-2
mn
2-3
1-0
3-0
nb
001-0
005
08-0
12
01-0
03
005-0
01
balance
iron
annealing
hour
1150
degree
-1200
cold
deforming
5-15
exhibits
dramatically
rupture
resistance
ductility
700
austenitic alloy
balance iron
alloy exhibits
resistant austenitic
creep resistant
temperature creep
improved creep
/420/148/