Salt-soda sinter process for recovering aluminum from fly ash
Patent
·
OSTI ID:863825
- Oak Ridge, TN
A method for recovering aluminum values from fly ash comprises sintering the fly ash with a mixture of NaCl and Na.sub.2 CO.sub.3 to a temperature in the range 700.degree.-900.degree. C. for a period of time sufficient to convert greater than 90% of the aluminum content of the fly ash into an acid-soluble fraction and then contacting the thus-treated fraction with an aqueous solution of nitric or sulfuric acid to effect dissolution of aluminum and other metal values in said solution.
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- DOE Contract Number:
- AC04-76
- Assignee:
- United States of America as represented by United States (Washington, DC)
- Patent Number(s):
- US 4254088
- OSTI ID:
- 863825
- Country of Publication:
- United States
- Language:
- English
Similar Records
Salt-soda sinter process for recovering aluminum from fly ash
Salt-soda sinter process for recovering aluminum from fly ash
Electrochemical study of Aluminum-Fly Ash composites obtained by powder metallurgy
Patent
·
Tue Mar 03 00:00:00 EST 1981
·
OSTI ID:863825
Salt-soda sinter process for recovering aluminum from fly ash
Patent
·
·
OSTI ID:863825
Electrochemical study of Aluminum-Fly Ash composites obtained by powder metallurgy
Journal Article
·
Sun Jul 15 00:00:00 EDT 2012
· Materials Characterization
·
OSTI ID:863825
+5 more
Related Subjects
salt-soda
sinter
process
recovering
aluminum
fly
ash
method
values
comprises
sintering
mixture
nacl
na
temperature
range
700
degree
-900
period
time
sufficient
convert
90
content
acid-soluble
fraction
contacting
thus-treated
aqueous
solution
nitric
sulfuric
acid
effect
dissolution
metal
metal values
time sufficient
fly ash
aqueous solution
sulfuric acid
recovering aluminum
comprises sintering
treated fraction
sinter process
/423/
sinter
process
recovering
aluminum
fly
ash
method
values
comprises
sintering
mixture
nacl
na
temperature
range
700
degree
-900
period
time
sufficient
convert
90
content
acid-soluble
fraction
contacting
thus-treated
aqueous
solution
nitric
sulfuric
acid
effect
dissolution
metal
metal values
time sufficient
fly ash
aqueous solution
sulfuric acid
recovering aluminum
comprises sintering
treated fraction
sinter process
/423/