Title: Glass-ceramic composition for hermetic seals

Abstract

The invention relates to a glass-ceramic composition having a high fracture strength adaptable for hermetically sealing to chromium bearing iron or nickel base alloys at temperatures of between about 950.degree. C to about 1100.degree. C to form a hermetically sealed insulator body, comprising from about 55 to about 65 weight percent SiO.sub.2, from about 0 to about 5 weight percent Al.sub.2 O.sub.3, from about 6 to about 11 weight % Li.sub.2 O, from about 25 to about 32 weight percent BaO, from about 0.5 to about 1.0 weight percent CoO and from about 1.5 to about 3.5 weight percent P.sub.2 O.sub.5.

Inventors:
 [1]
  1. (Albuquerque, NM)
Publication Date:
Research Org.:
Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
OSTI Identifier:
863269
Patent Number(s):
US 4135936
Assignee:
United States of America as represented by United States (Washington, DC)
DOE Contract Number:  
AT(29-1)-789
Resource Type:
Patent
Country of Publication:
United States
Language:
English
Subject:
glass-ceramic; composition; hermetic; seals; relates; fracture; strength; adaptable; hermetically; sealing; chromium; bearing; iron; nickel; base; alloys; temperatures; 950; degree; 1100; form; sealed; insulator; comprising; 55; 65; weight; percent; sio; 11; 25; 32; bao; coo; nickel base; hermetically sealing; base alloy; base alloys; ceramic composition; hermetically sealed; weight percent; hermetic seal; fracture strength; glass-ceramic composition; sealed insulator; hermetic seals; hermetically seal; /501/

Citation Formats

Ballard, Jr., Clifford P. Glass-ceramic composition for hermetic seals. United States: N. p., 1979. Web.
Ballard, Jr., Clifford P. Glass-ceramic composition for hermetic seals. United States.
Ballard, Jr., Clifford P. Mon . "Glass-ceramic composition for hermetic seals". United States. https://www.osti.gov/servlets/purl/863269.
@article{osti_863269,
title = {Glass-ceramic composition for hermetic seals},
author = {Ballard, Jr., Clifford P.},
abstractNote = {The invention relates to a glass-ceramic composition having a high fracture strength adaptable for hermetically sealing to chromium bearing iron or nickel base alloys at temperatures of between about 950.degree. C to about 1100.degree. C to form a hermetically sealed insulator body, comprising from about 55 to about 65 weight percent SiO.sub.2, from about 0 to about 5 weight percent Al.sub.2 O.sub.3, from about 6 to about 11 weight % Li.sub.2 O, from about 25 to about 32 weight percent BaO, from about 0.5 to about 1.0 weight percent CoO and from about 1.5 to about 3.5 weight percent P.sub.2 O.sub.5.},
doi = {},
url = {https://www.osti.gov/biblio/863269}, journal = {},
number = ,
volume = ,
place = {United States},
year = {1979},
month = {1}
}

Patent:

Save / Share: