Tungsten-nickel-cobalt alloy and method of producing same
- Los Alamos, NM
An improved tungsten alloy having a tungsten content of approximately 95 weight percent, a nickel content of about 3 weight percent, and the balance being cobalt of about 2 weight percent is described. A method for producing said tungsten-nickel-cobalt alloy is further described and comprises (a) coating the tungsten particles with a nickel-cobalt alloy, (b) pressing the coated particles into a compact shape, (c) heating said compact in hydrogen to a temperature in the range of 1400.degree. C and holding at this elevated temperature for a period of about 2 hours, (d) increasing this elevated temperature to about 1500.degree. C and holding for 1 hour at this temperature, (e) cooling to about 1200.degree. C and replacing the hydrogen atmosphere with an inert argon atmosphere while maintaining this elevated temperature for a period of about 1/2 hour, and (f) cooling the resulting alloy to room temperature in this argon atmosphere.
- Research Organization:
- Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)
- Assignee:
- United States of America as represented by United States Energy (Washington, DC)
- Patent Number(s):
- US 4012230
- OSTI ID:
- 862787
- Country of Publication:
- United States
- Language:
- English
Similar Records
High density tungsten-nickel-iron-cobalt alloys having improved hardness and method for making same
Method of improving fatigue life of cast nickel based superalloys and composition
Related Subjects
alloy
method
producing
improved
tungsten
content
approximately
95
weight
percent
nickel
balance
cobalt
described
comprises
coating
particles
nickel-cobalt
pressing
coated
compact
shape
heating
hydrogen
temperature
range
1400
degree
holding
elevated
period
hours
increasing
1500
hour
cooling
1200
replacing
atmosphere
inert
argon
maintaining
resulting
argon atmosphere
weight percent
elevated temperature
coated particles
hydrogen atmosphere
tungsten alloy
tungsten particles
resulting alloy
nickel content
/419/75/428/