Nondestructive evaluation of fatigue damage on low alloy steel by magnetomechanical acoustic emission technique
- Toshiba Corp., Yokohama (Japan)
A modified magnetomechanical acoustic emission (MAE) technique, denoted Pulse-MAE, in which the magnetization by current pulse was adopted, was newly developed and its applicability was assessed for the nondestructive detection and evaluation of fatigue damage in reactor pressure vessel steel SFVV2 and SA508 class2. MAE signals were measured with both conventional MAE and Pulse-MAE technique for fatigue damaged specimens having several damage fractions, and peak voltage ratio Vp/Vo, where Vp and Vo were the peak voltage for damaged and undamaged specimen respectively, was chosen as a measure. Vp/Vo was found to increase monotonously at the early stage of fatigue process and the rate of increase in Vp/Vo during the fatigue process was larger in Pulse-MAE than conventional MAE. Therefore, Pulse-MAE technique proved to have higher sensitivity for the detection of fatigue damage compared with the conventional MAE and to have the potential of a practical technique for nondestructive detection and evaluation of fatigue damage in actual components.
- OSTI ID:
- 86149
- Report Number(s):
- CONF-9505104-; ISBN 0-87170-548-6; TRN: 95:017438
- Resource Relation:
- Conference: 13. international conference on nondestructive evaluation in the nuclear and pressure vessel industries, Kyoto (Japan), 22-25 May 1995; Other Information: PBD: 1995; Related Information: Is Part Of Proceedings of the 13. international conference on NDE in the nuclear and pressure vessel industries; Iida, Kunihiro [ed.] [Shibaura Inst. of Technology, Tokyo (Japan)]; Light, G.M [ed.] [Southwest Research Inst., San Antonio, TX (United States)]; Whittle, M.J. [ed.] [John Whittle and Associates, Cheshire (United Kingdom)]; PB: 503 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Nondestructive evaluation of fatigue damage on low-alloy steel by magnetic technique
Monitoring fatigue damage in carbon fiber composites using an acoustic impact technique