Impermeable thin AI2O3 overlay for TBC protection from sulfate and vanadate attack in gas turbines
- University of Pittsburgh
25 {micro}m and a 2 {micro}m thick Al{sub 2}O{sub 3} overlay were deposited by HVOF thermal spray and by sol-gel coating method, respectively, onto to the surface of YSZ coating. Indenter test was employed to investigate the spalling of YSZ with and without Al{sub 2}O{sub 3} overlay after hot corrosion. The results showed that Al{sub 2}O{sub 3} overlay acted as a barrier against the infiltration of the molten salt into the YSZ coating during exposure, thus significantly reduced the amount of M-phase of ZrO{sub 2} in YSZ coating. Thick Al{sub 2}O{sub 3} overlay will increase compressive stress and failure in TBC. During next reporting time, Al{sub 2}O{sub 3} overlay will be deposited on the YSZ surface by the composite-sol-gel route (CSG). Hot corrosion tests will be carried out on the TBC.
- Research Organization:
- University of Pittsburgh
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- FC26-01NT41189
- OSTI ID:
- 850475
- Country of Publication:
- United States
- Language:
- English
Similar Records
IMPERMEABLE THIN Al2O3 OVERLAY FOR TBC PROTECTION FROM SULFATE AND VANADATE ATTACK IN GAS TURBINES
Impermeable thin AI2O3 overlay for TBC protection from sulfate and vanadate attack in gas turbines