Atomic scale structure of the 5-fold surface of an AlPdMn quasicrystal: A quantitative X-Ray photoelectron diffraction analysis
- LBNL Library
The atomic scale structure of the 5-fold symmetric surface of an AlPdMn quasicrystal is investigated quantitatively by comparing x-ray photoelectron diffraction (XPD) simulations to experiment. The observed 5-fold symmetry of the diffraction patterns indicates that the surface is quasicrystalline with no hint of a reconstruction from the bulk structure. In analyzing the experimental data, many possible bulk terminations have been tested. Those few that fit best to the data have in common that they contain an Al-rich surface layer followed by a dense mixed Al/Pd/Mn layer. These best terminations, while not identical to each other, are suggested to form terraces coexisting on a real surface. Structural relaxations of the quasicrystal surface are also analyzed: mixing several best-fit terminations gives average best-fit interlayer spacing changes of Dd12 = -0.057 Angstrom, Dd24 = +0.159 Angstrom. These results are in good agreement with a prior structure determination by LEED on a sample that was prepared in a different manner.
- Research Organization:
- Ernest Orlando Lawrence Berkeley National Laboratory, Berkeley, CA (US)
- Sponsoring Organization:
- USDOE Director. Office of Science. Office of Basic Energy Sciences. Materials Science and Engineering Division; Surface Science Lab of National University of Singapore, Lee Foundation. Singapore (US)
- DOE Contract Number:
- AC03-76SF00098
- OSTI ID:
- 834626
- Report Number(s):
- LBNL--52328
- Journal Information:
- Physical Review B, Journal Name: Physical Review B Vol. 69
- Country of Publication:
- United States
- Language:
- English
Similar Records
Formation of a well ordered ultrathin aluminum oxide film on icosahedral AlPdMn quasicrystal
Atomic Scale coexistence of Periodic and quasiperiodic order in a2-fold A1-Ni-Co decagonal quasicrystal surface