ISOBUTANOL-METHANOL MIXTURES FROM SYNTHESIS GAS

Technical Report · Tue Sep 01 04:00:00 EDT 1998

DOI:https://doi.org/10.2172/829615· OSTI ID:829615

Iglesia, Enrique

Isobutanol is potential as a fuel additive or precursor to methyl tert-butyl ether (MTBE). Alkali-promoted Cu/ZnO/Al{sub 2}O{sub 3} and Cu/MgO/CeO{sub 2} materials have been found to catalyze the formation of isobutanol from CO and H{sub 2} at temperatures (573-623 K) that allow their use in slurry reactors. Our studies focus on the mechanism and structural requirements for selective isobutanol synthesis on these types of catalysts. Alkali promoted Cu/MgO/CeO{sub 2}, Cu/MgO/ZnO, and CuZnAlO{sub x} materials and their individual components Cu/MgO, MgO/CeO{sub 2}, MgO and CeO{sub 2} have been prepared for the use in kinetic studies of alcohol coupling reactions, in identification of reaction intermediates, and in isobutanol synthesis at high pressures. These samples were prepared by coprecipitation of mixed nitrate solutions with an aqueous solution of KOH (2M) and K{sub 2}CO{sub 3} (1M) at 338 K at a constant pH of 9, except for Cs-Cu/ZnO/Al{sub 2}O{sub 3} at a pH of 7, in a well-stirred thermostated container. The precipitate was filtered, washed thoroughly with dioinized water at 303 K in order to remove residual K ions, and dried at 353 K overnight. Dried samples were calcined at 723 K, except for Cs-Cu/ZnO/Al{sub 2}O{sub 3} at 623 K, for 4 h in order to form the corresponding mixed oxides. Alkali addition (K or Cs) was performed by incipient wetness using K{sub 2}CO{sub 3} (0.25 M) and CH{sub 3}COOCs (0.25 M) aqueous solutions. The crystallinity and phase structures of resulting materials were analyzed by powered X-ray diffraction.

• Research Organization: University of California (US)
• Sponsoring Organization: (US)
• DOE Contract Number: AC22-94PC94066
• OSTI ID: 829615
• Country of Publication: United States
• Language: English

Related Subjects

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS
AQUEOUS SOLUTIONS
ETHYL ETHER
FUEL ADDITIVES
MIXTURES
REACTION INTERMEDIATES
SLURRY REACTORS
SYNTHESIS
SYNTHESIS GAS
X-RAY DIFFRACTION