Phase Stability of Chromium(III) Oxide Hydroxide in Alkaline Sodium Phosphate Solutions
Grimaldiite ({alpha}-CrOOH) is shown to transform to a sodium-chromium(III)-hydroxyphosphate compound (SCHP) in alkaline sodium phosphate solutions at elevated temperatures via CrOOH(s) + 4Na{sup +} + 2HPO{sub 4}{sup 2-} = Na{sub 4}Cr(OH)(PO{sub 4}){sub 2}(s) + H{sub 2}O. X-ray diffraction analyses indicate that SCHP possesses an orthorhombic lattice having the same space group symmetry (Ibam, No.72) as sodium ferric hydroxyphosphate. A structurally-consistent designation for SCHP is Na{sub 3}Cr(PO{sub 4}){sub 2} {center_dot} NaOH; the molar volume of SCHP is estimated to be 1552 cm{sup 3}. The thermodynamic equilibrium for the above reaction was defined in the system Na{sub 2}O-P{sub 2}O{sub 5}-Cr{sub 2}O{sub 3}-H{sub 2}O for Na/P molar ratios between 2.0 and 2.4. On the basis of observed reaction threshold values for sodium phosphate concentration and temperature, the standard molar entropy (S{sup o}), heat capacity (C{sub p}{sup o}) and free energy of formation ({Delta}G{sub f}{sup o}) for SCHP were calculated to be 690 J/(mol-K), 622 J/(mol-K) and -3509.97 kJ/mol, respectively.
- Research Organization:
- Lockheed Martin Corporation, Schenectady, NY 12301 (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC12-00SN39357
- OSTI ID:
- 821873
- Report Number(s):
- LM-03K071
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetite stability in aqueous sodium phosphate solutions at elevated temperatures
Titanium(IV) oxide phase stability in alkaline sodium phosphate solutions at elevated temperatures