Study of Fatigue and Fracture Behavior of Cr-Based Alloys and Intermetallic Materials
- ORNL
The microhardness, and tensile and fracture-toughness properties of drop-cast and directionally-solidified Cr-9.25 at.% (atomic percent) Ta alloys have been investigated. Directional solidification was found to soften the alloy, which could be related to the development of equilibrium and aligned microstructures. It was observed that the tensile properties of the Cr-Ta alloys at room and elevated temperatures could be improved by obtaining aligned microstructures. The directionally-solidified alloy also showed increased fracture toughness at room temperature. This trend is mainly associated with crack deflection and the formation of shear ribs in the samples with aligned microstructures. The sample with better-aligned lamellar exhibits greater fracture toughness.
- Research Organization:
- ORNL Oak Ridge National Laboratory (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 814431
- Report Number(s):
- ORNL/SUB/93-SP173/04
- Country of Publication:
- United States
- Language:
- English
Similar Records
Processing and Microstructures of Cr-Ta and Cr-Ta-Mo Composites Reinforced by the Cr2Ta Laves Phase
Fracture and fracture toughness of directionally solidified TiAl-based two-phase alloys
Microstructure, creep and fracture toughness of directionally solidified NiAl/(Cr,Mo) alloys modified with Hf, Si, Ta, Ti additions
Conference
·
Tue Apr 22 00:00:00 EDT 2003
·
OSTI ID:835705
Fracture and fracture toughness of directionally solidified TiAl-based two-phase alloys
Book
·
Tue Dec 30 23:00:00 EST 1997
·
OSTI ID:293140
Microstructure, creep and fracture toughness of directionally solidified NiAl/(Cr,Mo) alloys modified with Hf, Si, Ta, Ti additions
Conference
·
Thu Jul 01 00:00:00 EDT 1999
·
OSTI ID:20001635