Screw dislocations in GaN grown by different methods
- LBNL Library
A study of screw dislocations in Hydride-Vapor-Phase-Epitaxy (HVPE) template and Molecular-Beam-Epitaxy (MBE) over-layers was performed using Transmission Electron Microscopy (TEM) in plan-view and in cross-section. It was observed that screw dislocations in the HVPE layers were decorated by small voids arranged along the screw axis. However, no voids were observed along screw dislocations in MBE overlayers. This was true both for MBE samples grown under Ga-lean and Ga-rich conditions. Dislocation core structures have been studied in these samples in the plan-view configuration. These experiments were supported by image simulation using the most recent models. A direct reconstruction of the phase and amplitude of the scattered electron wave from a focal series of high-resolution images was applied. It was shown that the core structures of screw dislocations in the studied materials were filled. The filed dislocation cores in an MBE samples were stoichiometric. However, in HVPE materials, single atomic columns show substantial differences in intensities and might indicate the possibility of higher Ga concentration in the core than in the matrix. A much lower intensity of the atomic column at the tip of the void was observed. This might suggest presence of lighter elements, such as oxygen, responsible for their formation.
- Research Organization:
- Ernest Orlando Lawrence Berkeley National Laboratory, Berkeley, CA (US)
- Sponsoring Organization:
- U.S.DOE. Director, Office of Science. Basic Energy Sciences (US)
- DOE Contract Number:
- AC03-76SF00098
- OSTI ID:
- 813388
- Report Number(s):
- LBNL--52725
- Country of Publication:
- United States
- Language:
- English
Similar Records
Screw dislocations in GaN
Recombination-related properties of a-screw dislocations in GaN: A combined CL, EBIC, TEM study