Preventing vacuum leaks in the Continuous Electron Beam Accelerator Facility cavity pair bellows
Journal Article
·
· Journal of Vacuum Science Technology A
OSTI ID:801723
Occasional vacuum leaks have occurred in bellows assemblies of helium pressure vessels at the Continuous Electron Beam Accelerator Facility. The flanged stainless steel bellows assemblies are used to connect the niobium rf cavity pairs to the surrounding liquid helium pressure vessels. An investigation of the source of these leaks has revealed a through-thickness network of microcracks in the cuff weld zones. The cuff material contained a mixture of soft and very hard elongated intermetallic inclusions that were oriented parallel with the weld fusion line; these inclusions served as crack initiation sites. Surface-exposed inclusions, in contact with a chlorine residue from a postweld machining process, induced crevice corrosion during a year of storage. Residual stresses in the weld led to a combination of lamellar tearing and stress corrosion cracking. Propagation of the cracks from one inclusion to another resulted in continuous vacuum leakage paths from the primary (2 K) helium circuit to the vacuum insulation space. Additional vacuum leaks were prevented by reconfiguring the weld geometry and avoiding any processing with chlorinated substances.
- Research Organization:
- Thomas Jefferson National Accelerator Facility, Newport News, VA (US)
- Sponsoring Organization:
- USDOE Office of Energy Research (ER) (US)
- DOE Contract Number:
- AC05-84ER40150
- OSTI ID:
- 801723
- Report Number(s):
- CEBAF-PR-93-070; DOE/ER/40150-2210
- Journal Information:
- Journal of Vacuum Science Technology A, Journal Name: Journal of Vacuum Science Technology A Vol. 12
- Country of Publication:
- United States
- Language:
- English
Similar Records
Preventing vacuum leaks in the Continuous Electron Beam Accelerator Facility cavity pair bellows
BELLOWS FAILURE IN SOLIDS SEPARATION LOOP OF THE HRT MOCKUP
Reactor cooling water expansion joint bellows: The role of the seam weld in fatigue crack development
Journal Article
·
Thu Sep 01 00:00:00 EDT 1994
· Journal of Vacuum Science and Technology, A (Vacuum, Surfaces and Films); (United States)
·
OSTI ID:7082067
BELLOWS FAILURE IN SOLIDS SEPARATION LOOP OF THE HRT MOCKUP
Technical Report
·
Thu Jan 31 23:00:00 EST 1957
·
OSTI ID:4322319
Reactor cooling water expansion joint bellows: The role of the seam weld in fatigue crack development
Conference
·
Mon Nov 30 23:00:00 EST 1992
·
OSTI ID:10114664