Biaxially aligned template films fabricated by inclined-substrate deposition for YBCO-coated conductor applications.
Inclined substrate deposition (ISD) has the potential for rapid production of high-quality biaxially textured buffer layers, which are important for YBCO-coated conductor applications. We have grown biaxially textured MgO films by ISD at deposition rates of 20-100 {angstrom}/sec. Columnar grains with a roof-tile surface structure were observed in the ISD-MgO films. X-ray pole figure analysis revealed that the (002) planes of the ISD-MgO films are tilted at an angle from the substrate normal. A small {phi}-scan full-width at half maximum (FWHM) of {approx}9{sup o} was observed on MgO films deposited at an inclination angle of 55{sup o}. In-plane texture in the ISD MgO films developed in the first 0.5 {micro}m from the interface, then stabilized with further increases in film thickness. YBCO films deposited by pulsed laser deposition on ISD-MgO buffered Hastelloy C276 substrates were biaxially aligned with the c-axis parallel to the substrate normal. T{sub c} of 91 K with a sharp transition and transport J{sub c} of 5.5 x 10{sup 5} A/cm{sup 2} at 77 K in self-field were measured on a YBCO film that was 0.46-{micro}m thick, 4-mm wide, 10-mm long.
- Research Organization:
- Argonne National Lab., IL (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-31-109-ENG-38
- OSTI ID:
- 799836
- Report Number(s):
- ANL/ET/CP-106968; TRN: US200224%%271
- Resource Relation:
- Conference: Applied Superconductivity Conference and Expo (ASC 2002), Houston, TX (US), 08/04/2002--08/09/2002; Other Information: PBD: 12 Aug 2002
- Country of Publication:
- United States
- Language:
- English
Similar Records
Inclined-substrate deposition of biaxially aligned template films for YBCO-coated conductors.
Inclined substrate deposition of magnesium oxide for YBCO-coated conductors.