Enhanced Field Emission from Chemically Etched and Electropolished Broad-area Niobium
Electron field emission (FE) from broad-area metal surfaces is known to occur at a much lower electric field than predicted by the Fowler-Nordheim law. This enhanced field emission (EFE) presents a major impediment to high electric field operation in a variety of applications, e.g., in superconducting niobium radio-frequency cavities for particle accelerators, klystrons, and a wide range of high voltage vacuum devices. Therefore EFE has been the subject of wide fundamental research for years. Although micron or submicron particles are often observed at such EFE sites, the strength and number of emitting sites and the causes of EFE strongly depend on surface preparation and handling, and the physical mechanism of EFE remains unknown. To systematically investigate the sources of this emission and to evaluate the best available surface preparation techniques with respect to resulting field emission, a DC scanning field emission microscope (SFEM) has been built at Thomas Jefferson National Accelerator Facility (Jefferson Lab). Broad-area samples can be moved laterally in a raster pattern (2.5 mu-m step resolution) under a high voltage micro-tip for EFE detection and localization in the SFEM. The emitting sites can then be characterized by SEM and EDX without breaking ultra high vacuum. EFE sources from planar Nb have been studied after preparation by chemical etching and electropolishing combined with ultrasonic deionized water rinse (UWR). Emitters have been identified and analyzed, and the preparation process has been refined and improved based on scan results. With the improved preparation process, field-emission-free or near field-emission-free surfaces at -140 MV/m have been achieved consistently on a number of samples.
- Research Organization:
- Thomas Jefferson National Accelerator Facility (TJNAF), Newport News, VA (United States)
- Sponsoring Organization:
- USDOE Office of Energy Research (ER) (US)
- DOE Contract Number:
- AC05-84ER40150
- OSTI ID:
- 798735
- Report Number(s):
- JLAB-ACC-02-08; DOE/ER/40150-2129; TRN: US0202054
- Resource Relation:
- Other Information: No journal information given for this preprint; PBD: 1 Aug 2002
- Country of Publication:
- United States
- Language:
- English
Similar Records
DC Scanning Field Emission Microscope Integrated with Existing Scanning Electron Microscope
Direct current scanning field emission microscope integrated with existing scanning electron microscope