Glass Formulation Development for INEEL Sodium -Bearing Waste (FY2001 WM-180)
A systematic study was undertaken to develop a glass composition to demonstrate the vitrification flowsheet of the Idaho National Engineering and Environmental Laboratory's sodium bearing waste (SBW) using the latest WM-180 tank composition. Although the previous study did not restrict waste loadings (WLs) based on the potential to form a segregated salt layer, avoiding its development in a melter is beneficial and was the primary focus from the glass-formulation perspective. The testing results described in this report were aimed at providing a candidate glass composition for use in a scaled melter demonstration of direct vitrification of WM-180 in the Research Scale Melter (RSM) at Pacific Northwest National Laboratory and the EV-16 melter at the Clemson Environmental Technology Laboratory.
- Research Organization:
- Savannah River Site (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC09-96SR18500
- OSTI ID:
- 786671
- Report Number(s):
- WSRC-TR-2001-00295
- Country of Publication:
- United States
- Language:
- English
Similar Records
GLASS FORMULATION FOR INEEL SODIUM BEARING WASTE
Test Summary Report INEEL Sodium-Bearing Waste Vitrification Demonstration RSM-01-1
Test Summary Report INEEL Sodium-Bearing Waste Vitrification Demonstration RSM-01-1
Conference
·
Wed Oct 30 23:00:00 EST 2002
·
OSTI ID:992030
Test Summary Report INEEL Sodium-Bearing Waste Vitrification Demonstration RSM-01-1
Technical Report
·
Mon May 21 00:00:00 EDT 2001
·
OSTI ID:787349
Test Summary Report INEEL Sodium-Bearing Waste Vitrification Demonstration RSM-01-1
Technical Report
·
Mon May 21 00:00:00 EDT 2001
·
OSTI ID:965672