Normal and anomalous yield stresses in a TiAl single crystal and the dominating dislocation mechanisms
Book
·
OSTI ID:78386
- Univ. of Oxford (United Kingdom). Dept. of Material
Single crystal {gamma}-TiAl with axial orientation [{bar 3} 16 15] has been tested in compression between 4K and 1,048K and the dislocation structures observed in TEM. The slip plane was found to be (111) over the entire temperature range tested. Three regimes exist in the variation of the yield stress with temperature, whereas the dislocation substructures are of two types, dominated by 30{degree} 1/3[11{bar 2}] and 1/2 {l_angle}110] dislocations respectively. The anomalous yield stress is associated with 1/2{l_angle}110] dislocations undergoing frequent cross-slip off the (111) plane.
- OSTI ID:
- 78386
- Report Number(s):
- CONF-941144--; ISBN 1-55899-265-0
- Country of Publication:
- United States
- Language:
- English
Similar Records
Dynamic Dislocation Mechanisms For the Anomalous Slip in a Single-Crystal BCC Metal Oriented for "Single Slip"
Creep of anomalous Ni{sub 3}Ga
Low temperature deformation and dislocation substructure of ruthenium aluminide polycrystals
Technical Report
·
Wed Jan 10 23:00:00 EST 2007
·
OSTI ID:900046
Creep of anomalous Ni{sub 3}Ga
Book
·
Tue Dec 30 23:00:00 EST 1997
·
OSTI ID:571882
Low temperature deformation and dislocation substructure of ruthenium aluminide polycrystals
Journal Article
·
Thu Feb 04 23:00:00 EST 1999
· Acta Materialia
·
OSTI ID:329090