Fracture toughness, fracture planes and BDT in stoichiometric FeAl and NiAl single crystals
Book
·
OSTI ID:78322
- MPI fuer Eisenforschung GmbH, Duesseldorf (Germany)
Fracture toughness data of stoichiometric FeAl and NiAl single crystals were measured in fourpoint-bending tests and the crystallographic orientations of the resultant fracture surfaces were determined. For FeAl single crystals unexpectedly high fracture toughness values were measured even at low temperatures (17 MPa{radical}m at 77K). However, these crystals failed in a brittle manner for temperatures up to 300K. The crystallographic orientation of the fracture surfaces were strongly dependent on the environment due to hydrogen embrittlement. The NiAl specimens were precracked and the fracture toughness was measured in the weakest crystal orientation. The fracture surfaces were similar to those obtained in previous investigations. Although the room temperature (RT) K{sub IC}-value was the highest for pure weak-oriented NiAl (7.5 MPa{radical}m) the BDT temperature was found in the same region where it occurs for the hard orientation (673K to 693K). The onset of the BDT will be discussed.
- OSTI ID:
- 78322
- Report Number(s):
- CONF-941144--; ISBN 1-55899-265-0
- Country of Publication:
- United States
- Language:
- English
Similar Records
Room temperature fracture of FeAl and NiAl
Fracture toughness and microstructure of NiAl-based composite with TiC reinforcement
Microstructures from a directionally solidified NiAl-Cr eutectic deformed at room temperature
Journal Article
·
Tue Oct 01 00:00:00 EDT 1991
· Materials Performance; (United States)
·
OSTI ID:7088806
Fracture toughness and microstructure of NiAl-based composite with TiC reinforcement
Book
·
Tue Aug 01 00:00:00 EDT 1995
·
OSTI ID:78375
Microstructures from a directionally solidified NiAl-Cr eutectic deformed at room temperature
Journal Article
·
Fri Apr 15 00:00:00 EDT 1994
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:5188318