Combustion synthesis of TiC-based materials: Mechanisms, densification, and properties
- Univ. of California, San Diego, CA (United States)
The micromechanisms involved in the combustion synthesis of a Ti-C-Ni-Mo mixture resulting in the formation of a TiC-based composite were examined using the combustion wave quenching technique developed by Rogachev et al. At the micron level, the main reaction occurs at the interface between a Ti-Ni-C melt and C particles, resulting in the formation of a solid TiC{sub x} layer on the C particles. This layer undergoes a successive process of rapid growth and decomposition into TiC{sub x} spherules until all of the C particle is consumed. This mechanism is consistent with the apparent activation energy (E = 100 kJ/mol) for the process obtained from a macrokinetic investigation of the system. The apparent uniformity in size (d = 1 {mu}m) of the TiC{sub x} spherules upon formation indicates a critical condition in the stability of the energetics involved in the process. These TiC{sub x} spherules undergo growth due to Ostwald ripening and coalescence mechanisms resulting in a final apparent size of 2.5 {mu}m. For the compositions investigated, the addition of Mo did not affect either the micromechanisms or macrokinetics of the combustion synthesis process. Densification of the porous body after the combustion synthesis process can be carried out while it is still in a easily deformable state. The highly porous body is densified by a combination of fracture (communition), plastic deformation, and sintering. The mechanisms are identified for the case of combustion synthesized TiC. Mechanical properties and microstructures of a number of materials (e.g. TiC, TiB{sub 2}, Al{sub 2}O{sub 3}-TiB{sub 2}, TiB{sub 2}-SiC, TiC-Ni-Mo) produced by combustion synthesis combined with a high-velocity forging step are reviewed.
- OSTI ID:
- 77976
- Report Number(s):
- CONF-950201--; ISBN 0-87339-283-3
- Country of Publication:
- United States
- Language:
- English
Similar Records
Combustion synthesis in the Ti-C-Ni-Mo system. Part 2: Analysis
Combustion synthesis and densification of TiC-TiB{sub 2} and TiC-WC powders