X-Ray Powder Diffraction Study of Synthetic Palmierite, K{sub 2}Pb(SO{sub 4}){sub 2}
- Sandia National Laboratories
Palmierite (K{sub 2}Pb(SO{sub 4}){sub 2}) has been prepared via a chemical synthesis method. Intensity differences were observed when X-ray powder data from the newly synthesized compound were compared to the published powder diffraction card (PDF) 29-1015 for Palmierite. Investigation of these differences indicated the possibility of preferred orientation and/or chemical inhomogeneity affecting intensities, particularly those of the basal (00{ell}) reflections. Annealing of the Palmierite was found to reduce the effects of preferred orientation. Electron microprobe analysis confirmed K:Pb:S as 2:1:2 for the annealed Palmierite powder. Subsequent least-squares refinement and Rietveld analysis of the annealed powder showed peak intensities very close to that of a calculated Palmierite pattern (based on single crystal data), yet substantially higher than many of the PDF 29-1015 published intensities. Further investigation of peak intensity variation via calculated patterns suggested that the intensity discrepancies between the annealed sample and those found in PDF 29-1015 were potentially due to chemical variation in the K{sub 2}Pb(SO{sub 4}){sub 2} composition. X-ray powder diffraction and crystal data for Palmierite are reported for the annealed sample. Palmierite is Trigonal/Hexagonal with unit cell parameters a = 5.497(1){angstrom}, c = 20.864(2) {angstrom}, space group R-3m (166), and Z = 3.
- Research Organization:
- Sandia National Labs., Albuquerque, NM (US); Sandia National Labs., Livermore, CA (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 772052
- Report Number(s):
- SAND2000-3189J
- Journal Information:
- Powder Diffraction, Journal Name: Powder Diffraction
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure of LiAl[sub 2](OH)[sub 7][center dot]2H[sub 2]O