Comparison of the electrochemical properties of several commercial graphites with a templated disordered carbon
Conference
·
OSTI ID:754473
A templated carbon was prepared by the pyrolysis of pyrene impregnated into pillared clay (PILC). The electrochemical performance of this was evaluated with the goal of using this material as an anode in Li-ion cells. The reversible capacity was measured as a function of C rate and the cycling characteristics were determined for various intercalation protocols. The performance of this material was compared to that of several commercial graphites tested under the same conditions. The PILC carbon shows great promise as a Li-ion anode if the fade and first-cycle losses can be controlled.
- Research Organization:
- Argonne National Lab., IL (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 754473
- Report Number(s):
- ANL/CHM/CP-100694
- Country of Publication:
- United States
- Language:
- English
Similar Records
Comparison of the electrochemical properties of several commercial graphites with a templated disordered carbon
Small angle neutron and X-ray scattering studies of carbons prepared using inorganic templates
Small angle neutron scattering characterization of the porous structure of carbons prepared using inorganic templates
Conference
·
Tue Mar 21 23:00:00 EST 2000
·
OSTI ID:752627
Small angle neutron and X-ray scattering studies of carbons prepared using inorganic templates
Conference
·
Mon Sep 01 00:00:00 EDT 1997
·
OSTI ID:570137
Small angle neutron scattering characterization of the porous structure of carbons prepared using inorganic templates
Journal Article
·
Sun Jan 31 23:00:00 EST 1999
· Chemistry of Materials
·
OSTI ID:329067