In situ XAFS of the Li{sub x}Ni{sub 0.8}Co{sub 0.2} cathode for lithium-ion batteries
Conference
·
OSTI ID:751884
The layered LiNi{sub 0.8}Co{sub 0.2}O{sub 2} system is being considered as a new cathode material for the lithium-ion battery. Compared with LiCoO{sub 2}, the standard cathode formulation, it possesses improved electrochemical performance at a projected lower cost. In situ x-ray absorption fine-structure spectroscopy (XAFS) measurements were conducted on a cell cycled at a moderate rate and normal Li-ion operating voltages (3.0--4.1 V). The XAFS data collected at the Ni and Co edges approximately every 30 min. revealed details about the response of the cathode to Li insertion and extraction. These measurements on the Li{sub x}Ni{sub 0.8}Co{sub 0.2}O{sub 2} cathode (0.29 < x < 0.78) demonstrated the excellent reversibility of the cathode's short-range structure. However, the Co and Ni atoms behaved differently in response to Li insertion. This study corroborates previous work that explains the XAFS of the Ni atoms in terms of a Ni{sup 3+} Jahn-Teller ion. An analysis of the metal-metal distances suggests, contrary to a qualitative analysis of the x-ray absorption near-edge structure (XANES), that the Co{sup 3+} is oxidized to the maximum extent possible (within the Li content range of this experiment) at x = 0.47 {+-} 0.04, and further oxidation occurs at the Ni site.
- Research Organization:
- Argonne National Lab., IL (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 751884
- Report Number(s):
- ANL/CMT/CP-100890
- Country of Publication:
- United States
- Language:
- English
Similar Records
X-ray absorption spectroscopy studies of the Ni ion of Li(Ni{sub 0.8}Co{sub 0.15}Al{sub 0.05}){sub 0.8}(Ni{sub 0.5}Mn{sub 0.5}){sub 0.2}O{sub 2} with a core–shell structure and LiNi{sub 0.8}Co{sub 0.15}Al{sub 0.05}O{sub 2} as cathode materials
Surface changes on LiNi{sub 0.8}Co{sub 0.2}O{sub 2} particles during testing of high-power lithium-ion cells.
On the Li{sub x}Ni{sub 0.8}Co{sub 0.2}O{sub 2} system
Journal Article
·
Mon Oct 15 00:00:00 EDT 2012
· Materials Research Bulletin
·
OSTI ID:22215505
Surface changes on LiNi{sub 0.8}Co{sub 0.2}O{sub 2} particles during testing of high-power lithium-ion cells.
Journal Article
·
Thu Aug 01 00:00:00 EDT 2002
· Electrochem. Commun.
·
OSTI ID:949700
On the Li{sub x}Ni{sub 0.8}Co{sub 0.2}O{sub 2} system
Journal Article
·
Sat Feb 14 23:00:00 EST 1998
· Journal of Solid State Chemistry
·
OSTI ID:642192