Study of diffusion bond development in 6061 aluminum and its relationship to future high density fuels fabrication.
Powder metallurgy dispersions of uranium alloys and silicides in an aluminum matrix have been developed by the RERTR program as a new generation of proliferation-resistant fuels. Testing is done with miniplate-type fuel plates to simulate standard fuel with cladding and matrix in plate-type configurations. In order to seal the dispersion fuel plates, a diffusion bond must exist between the aluminum coverplates surrounding the fuel meat. Four different variations in the standard method for roll-bonding 6061 aluminum were studied. They included mechanical cleaning, addition of a getter material, modifications to the standard chemical etching, and welding methods. Aluminum test pieces were subjected to a bend test after each rolling pass. Results, based on 400 samples, indicate that at least a 70% reduction in thickness is required to produce a diffusion bond using the standard rollbonding method versus a 60% reduction using the Type II method in which the assembly was welded 100% and contained open 9mm holes at frame corners.
- Research Organization:
- Argonne National Lab., IL (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 750439
- Report Number(s):
- ANL/ET/CP-94634
- Country of Publication:
- United States
- Language:
- English
Similar Records
Thermal compatibility studies of unirradiated uranium silicide dispersed in aluminum. [Reduced Enrichment for Research and Test Reactor]
Development and compatibility of magnesium matrix fuel plates clad with 6061 aluminum alloy.