High temperature vacuum-annealing system
A system is described for use in homogenizing poly- and single-crystal metal samples at temperatures up to about 1300/sup 0/C. The furnace tube may be evacuated to a dynamic vacuum of 10/sup -3/ to 10/sup -4/ torr. A provision exists for pushing the sample from the hot zone into a zone the walls of which are at room temperature.
- Research Organization:
- Ames Lab., Iowa (USA); Iowa State Univ. of Science and Technology, Ames (USA)
- DOE Contract Number:
- W-7405-ENG-82
- OSTI ID:
- 7364499
- Report Number(s):
- IS-3765
- Country of Publication:
- United States
- Language:
- English
Similar Records
Vacuum annealing of zirconium based articles
LABORATORY VACUUM FURNACE FOR TEMPERATURES OF 2000-2500
HIGH TEMPERATURE HIGH VACUUM RESISTANCE FURNACE
Patent
·
Mon Jan 12 23:00:00 EST 1987
·
OSTI ID:6986699
LABORATORY VACUUM FURNACE FOR TEMPERATURES OF 2000-2500
Journal Article
·
Mon Dec 31 23:00:00 EST 1956
· Zavodskaya Lab.
·
OSTI ID:4342004
HIGH TEMPERATURE HIGH VACUUM RESISTANCE FURNACE
Journal Article
·
Sun May 01 00:00:00 EDT 1960
· Rev. Sci. Instr.
·
OSTI ID:4186851
Related Subjects
36 MATERIALS SCIENCE
360101* -- Metals & Alloys-- Preparation & Fabrication
42 ENGINEERING
420200 -- Engineering-- Facilities
Equipment
& Techniques
ANNEALING
CRYSTALS
DESIGN
DISPERSIONS
ELEMENTS
FURNACES
HEAT TREATMENTS
HOMOGENEOUS MIXTURES
METALS
MIXTURES
MONOCRYSTALS
POLYCRYSTALS
TUBES
VACUUM FURNACES
VERY HIGH TEMPERATURE
360101* -- Metals & Alloys-- Preparation & Fabrication
42 ENGINEERING
420200 -- Engineering-- Facilities
Equipment
& Techniques
ANNEALING
CRYSTALS
DESIGN
DISPERSIONS
ELEMENTS
FURNACES
HEAT TREATMENTS
HOMOGENEOUS MIXTURES
METALS
MIXTURES
MONOCRYSTALS
POLYCRYSTALS
TUBES
VACUUM FURNACES
VERY HIGH TEMPERATURE