Optical materials characterization. Semi-annual technical rport, 1 August 1976--31 January 1977

Technical Report · Mon Feb 28 23:00:00 EST 1977

OSTI ID:7307715

Feldman, A; Horowitz, D; Waxler, R M

The refractive indices of three prisms of chemical vapor deposited ZnS were measured at room temperature over the wavelength range 540 nm to 1.083 micrometers. The refractive indices of eight specimens of CaF/sup 2/ doped with Er were measured from 404.7 nm to 1.083 micrometers. The doping range was 0.001% to 3% Er. Interferometric measurements of dn/dT were made over the temperature range -180C to 200C at the wavelengths 632.8 nm and 3.39 micrometers on single crystal specimens of BaF/sup 2/, CaF/sup 2/, reactive atmosphere processed (RAP) KBr, RAP KCl, KCl doped with KI, LiF, NaF and SrF/sup 2/, and on chemical vapor deposited (CVD) ZnSe and hot forged CaF/sup 2/.

• Research Organization: National Bureau of Standards, Washington, DC (USA)
• OSTI ID: 7307715
• Report Number(s): PB-264692; NBSIR-77-1219
• Country of Publication: United States
• Language: English

Related Subjects

42 ENGINEERING
420300* -- Engineering-- Lasers-- (-1989)
ALKALI METAL COMPOUNDS
ALKALINE EARTH METAL COMPOUNDS
BARIUM COMPOUNDS
BARIUM FLUORIDES
BROMIDES
BROMINE COMPOUNDS
CALCIUM COMPOUNDS
CALCIUM FLUORIDES
CALCIUM HALIDES
CHALCOGENIDES
CHEMICAL COATING
CHEMICAL VAPOR DEPOSITION
CHLORIDES
CHLORINE COMPOUNDS
DEPOSITION
DOPED MATERIALS
FLUORIDES
FLUORINE COMPOUNDS
HALIDES
HALOGEN COMPOUNDS
INORGANIC PHOSPHORS
LASER MATERIALS
LASERS
OPTICAL PROPERTIES
PHOSPHORS
PHYSICAL PROPERTIES
POTASSIUM BROMIDES
POTASSIUM CHLORIDES
POTASSIUM COMPOUNDS
REFRACTIVITY
SULFIDES
SULFUR COMPOUNDS
SURFACE COATING
ZINC COMPOUNDS
ZINC SULFIDES