Vanadium and columbium additions in pressure vessel steels
- Lehigh Univ., Bethlehem, PA (United States). ATLSS Center
A statistically designed series of vanadium and columbium microalloyed C-Mn HSLA steels was used for an investigation of heat-affected zone (HAZ) toughness in post weld heat treated (PWHT) multi-pass welds. The vanadium additions were in the range 0.005 to 0.097 Wt.% and the columbium additions were in the range 0.004 to 0.06 Wt.% GMAW processes with welding heat inputs of 3kJ/mm and 5kJ/mm and post-weld heat treatments at 620 C for 2 10 hours were employed. A degradation of the HAZ toughness with additions of microalloy elements V and Cb in the as-welded and PWHT conditions was revealed. The 50 Joule (37 ft-lb) transition temperature (TT50J) for HAZs in all weld conditions correlated with maximum HAZ hardness. Increases in HAZ hardness and TT50J caused by PWHT were observed. Hence PWHT in some situations may not beneficial for V/Cb microalloyed HLSA steels. The randomly distributed precipitation of V and Cb carbides (V, Cb)C, including dislocation precipitation and matrix precipitation with particle sizes of 5--15 nm, is the predominant alloy carbide precipitate morphology in these steels. The crack initiation sites in Charpy specimens of HAZs tested at the approximate transition temperature are shifted from the highest stress triaxiality, mid-specimen location to an off center higher hardness location. This is found to be characteristic of fracture in the multipass HAZ of the microalloyed steel.
- OSTI ID:
- 72655
- Journal Information:
- Bulletin - Welding Research Council, Journal Issue: 395; Other Information: PBD: Sep 1994
- Country of Publication:
- United States
- Language:
- English
Similar Records
Physical metallurgical basis for heat-affected zone and base-plate properties of a microalloyed HSLA steel. Final report 1984-1986
Thermal stability of TiN in CGHAZ of nitrogen-enhanced HSLA steels