The effect of low Au concentrations on the properties of eutectic Sn/Pb
This study was of the effects moderately low Au concentrations ({le} 10 wt%) have on the mechanical properties and microstructure of an eutectic Sn/Pb alloy. Vibration (60--90 Hz swept sine wave for 30 hours) and thermal cycling (0--110C for 1450 cycles) reliability tests were performed on fine pitch leaded chip carriers using eutectic Sn/Pb solder on PCBs (printed circuit boards) with 0, 5, 10, 20, and 50{mu}in nominal Au thicknesses. Testing was also performed on double shear creep specimens consisting of arrays of regular pitch joints. There was a dramatic increase in the number of joints containing voids with increasing Au concentration, an effect more pronounced in the creep joints than in the reliability joints. These voids tended to coalesce and grow during rework simulation of the reliability joints. AuSn{sub 4} intermetallics present in toe of 4.8 wt% (50 {mu}in) Au vibration joints rotated from initial vertical perpendicular to surface of PCB metallization, solidification positions to roughly horizontal (parallel to plating surface) orientations during rework simulation and during aging of the parts. The AuSn{sub 4} intermetallics in the toe of the 4.8 wt% (50{mu}in) Au reflowed joints also rotated after vibration testing. No joint failures were observed in either vibration tested or thermally cycled specimens. Cracks formed in some of the vibration tested specimen joints under the heel of the gull-wing lead at Pb-rich phases. Thermally cycled specimens showed eutectic microstructure and intermetallic coarsening without crack formation. Creep tests showed loss of the superplasticity in eutectic Sn/Pb alloys with even the lowest Au concentration tested of 0.2 wt% Au. Intermetallic rotation was not a factor in crack propagation, but void presence was. Cracks tended to form in joints containing voids before forming in void-free joints. Crack propagation followed Sn/Sn grain boundaries and Sn/Pb phase boundaries from Pb-rich phase to Pb-rich phase.
- Research Organization:
- Lawrence Berkeley Lab., CA (United States)
- Sponsoring Organization:
- DOE; USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC03-76SF00098
- OSTI ID:
- 7253786
- Report Number(s):
- LBL-32390; ON: DE92041206
- Country of Publication:
- United States
- Language:
- English
Similar Records
The effect of low gold concentrations on the creep of eutectic tin-lead joints
Research on the mechanism of thermal fatigue in near-eutectic Pb-Sn solders
Related Subjects
360100* -- Metals & Alloys
42 ENGINEERING
426000 -- Engineering-- Components
Electron Devices & Circuits-- (1990-)
ALLOYS
CRACK PROPAGATION
CREEP
CRYSTAL STRUCTURE
DEPOSITION
DIMENSIONS
ELECTRONIC CIRCUITS
EUTECTICS
FABRICATION
GOLD ALLOYS
INTERMETALLIC COMPOUNDS
JOINING
JOINTS
LEAD ALLOYS
MECHANICAL PROPERTIES
MECHANICAL VIBRATIONS
METALLURGICAL FLUX
MICROSTRUCTURE
PLATING
PRINTED CIRCUITS
SOLDERED JOINTS
SOLDERING
SURFACE COATING
THERMAL CYCLING
THICKNESS
TIN ALLOYS
WELDING