Investigation of a new type of Al{sub 3}Ti-based L1{sub 2} alloy with second phase precipitation
Book
·
OSTI ID:72522
- Shanghai Jiao Tong Univ. (China). Dept. of Materials Science
Since the L1{sub 2} structured Al{sub 3}Ti alloy exists only in a narrow compositional range, further alloying of the single phase L1{sub 2} alloy to improve its property seems hardly successful. Developing two-phase or multiphase Al{sub 3}Ti alloys may be an effective approach for strengthening and toughening. In this article, a new type of Al{sub 3}Ti-based alloy which has a L1{sub 2} matrix with precipitates of a second phase is reported. The quaternary alloys based on Al{sub 67}Mn{sub 8}Ti{sub 25}, and modified with Nb additions, consist of an L1{sub 2} matrix and DO{sub 22} second phase particles in the annealed state, but the second phase can be dissolved by solution treatment and precipitated during high temperature aging. Remarkable strengthening and promising compressive ductility were exhibited by the experimental alloy. The influence of composition on the microstructure and properties of the alloys are reported also.
- OSTI ID:
- 72522
- Report Number(s):
- CONF-941144--; ISBN 1-55899-265-0
- Country of Publication:
- United States
- Language:
- English
Similar Records
Precipitation strengthening, yield stress anomaly and strain rate sensitivity of an L1{sub 2}-ordered intermetallic (Ni, Co){sub 3}(Al, Ti) alloy
Microstructure and mechanical properties of the L1{sub 2}/L2{sub 1} two-phase alloys in the quaternary Co-Al-Ni-Ti system
Structures of melt-spun and high-energy ball milled Al{sub 3}Ti-Mn-Nb intermetallic alloy
Journal Article
·
Tue Oct 13 00:00:00 EDT 1998
· Scripta Materialia
·
OSTI ID:20023126
Microstructure and mechanical properties of the L1{sub 2}/L2{sub 1} two-phase alloys in the quaternary Co-Al-Ni-Ti system
Book
·
Sat Jul 01 00:00:00 EDT 1995
·
OSTI ID:72562
Structures of melt-spun and high-energy ball milled Al{sub 3}Ti-Mn-Nb intermetallic alloy
Journal Article
·
Thu Dec 14 23:00:00 EST 1995
· Scripta Metallurgica et Materialia
·
OSTI ID:136953