Fatigue resistance of unnotched and post impact(+/- 30 deg/0 deg) 3-D braided composites. Final report
The fatigue resistance of a multiaxial braided (3-D) graphite/expoxy composite in both unnotched and post impacted conditions has been evaluated. The material tested is a (+/- 30/0 deg) multiaxial braid constructed from AS4/12K tow graphite fibers and British Petroleum E905L epoxy resin. These materials were braided as dry preforms and the epoxy was added using a resin transfer molding process (RTM). The unnotched and post-impact specimens were tested in compression-compression fatigue at 10 Hz with a stress ratio of R=10. The unnotched tension-tension fatigue specimens were tested at S Hz with a stress ration of R=0.1. Damage initiation and growth was documented through the application of radiography and ultrasonic through transmission (C-scans). Visible inspection of surface and edge damage was also noted to describe the initiation and progression of damage in these materials. The mechanisms leading to damage initiation were established and failure modes were determined. Stiffness and strength degradation were measured as a function of applied cycles. These 3-D braided composite results were compared to strain levels currently used to design primary structure in commercial aircraft composite components made from prepreg tape and autoclave cured.
- Research Organization:
- Lockheed Engineering and Sciences Co., Hampton, VA (United States)
- OSTI ID:
- 7198147
- Report Number(s):
- N-94-27433; NASA-CR-191590; NAS-1.26:191590; CNN: NAS1-19000; RTOP 510-02-12-09
- Country of Publication:
- United States
- Language:
- English
Similar Records
Characterization and prediction of post-impact fatigue damage in stitched composites. Ph.D. Thesis
Post-impact fatigue of cross-plied, through-the-thickness reinforced carbon/epoxy composites. M.S. Thesis - Clemson Univ.