Direct observation of the primary state of damage in ion-irradiated platinum and tungsten. Report No. 4300
The primary state of damage in platinum and tungsten caused by ions of varying mass and energy, was investigated using the field ion microscope (FIM). The damage could be classified into three morphological types: (a) depleted zones (DZs); (b) voids; (c) dislocation loops. Platinum specimens of 99.999% purity were irradiated in situ at 60 K with 20 keV Kr/sup +/ ions to a dose of (3 to 5) x 10/sup 12/ ion cm/sup -2/ and examined by the pulse field-evaporation technique at 60 K. The experimental conditions were created such that each depleted zone was created by a single incident ion. All three morphological types were observed.
- Research Organization:
- Cornell Univ., Ithaca, NY (USA). Materials Science Center
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AS02-76ER01358
- OSTI ID:
- 7150933
- Report Number(s):
- DOE/ER/03158-92; TRN: 80-018694
- Resource Relation:
- Other Information: Thesis
- Country of Publication:
- United States
- Language:
- English
Similar Records
Direct observation of the primary state of damage in ion-irradiated platinum and tungsten
Direct observations of the primary state of radiation damage of ion-irradiated tungsten and platinum
Direct observation of the primary state of damage of ion-irradiated tungsten: I. Three-dimensional spatial distribution of vacancies
Thesis/Dissertation
·
Tue Jan 01 00:00:00 EST 1980
·
OSTI ID:7150933
Direct observations of the primary state of radiation damage of ion-irradiated tungsten and platinum
Conference
·
Tue Jul 01 00:00:00 EDT 1980
·
OSTI ID:7150933
+1 more
Direct observation of the primary state of damage of ion-irradiated tungsten: I. Three-dimensional spatial distribution of vacancies
Technical Report
·
Wed Oct 01 00:00:00 EDT 1980
·
OSTI ID:7150933