Crystal orientation dependence of elastic precursor strength in pentaerythritol tetranitrate
- Group M-7, Los Alamos National Laboratory, MS P952 Los Alamos, New Mexico 87545 (United States)
Elastic precursor shock strengths were measured using VISAR instrumentation on pentaerythritol tetranitrate crystals 2.9 to 6.4 mm thick. Input shock strength was 1.2 GPa. A factor of 3 difference in elastic shock strength and a factor of 2 difference in critical resolved shear stress were observed depending on the crystal orientation. The order of increasing elastic shock strength was [100], [101], [110], and [001]. This is the same order as that obtained in our analysis for increasing steric hindrance to shear, indicating that the relative strength of different orientations of this molecular crystal under shock conditions is governed by steric hindrance to shear. [copyright]American Institute of Physics
- OSTI ID:
- 7017278
- Report Number(s):
- CONF-921145-; CODEN: APCPCS
- Journal Information:
- AIP Conference Proceedings (American Institute of Physics); (United States), Vol. 309:1; Conference: Production and neutralization of negative ions and beams, Upton, NY (United States), 9-13 Nov 1992; ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Molecular mechanics modeling of shear and the crystal orientation dependence of the elastic precursor shock strength in pentaerythritol tetranitrate
Anomalous shock initiation of detonation in pentaerythritol tetranitrate crystals
Related Subjects
PETN
SHOCK WAVES
ELASTICITY
ORIENTATION
PLASTICITY
SHEAR PROPERTIES
STEREOCHEMISTRY
VERY HIGH PRESSURE
CHEMICAL EXPLOSIVES
ESTERS
EXPLOSIVES
MECHANICAL PROPERTIES
NITRATES
NITRIC ACID ESTERS
NITROGEN COMPOUNDS
ORGANIC COMPOUNDS
OXYGEN COMPOUNDS
TENSILE PROPERTIES
360603* - Materials- Properties