Room temperature moisture kinetics of Kevlar 49 fabric/epoxy laminates

Conference · Sun Jan 01 04:00:00 EST 1978

OSTI ID:6935563

Allred, R E; Lindrose, A M

Hygrothermal effects can significantly influence the failure behavior of high performance epoxy-based composites. As such, it is necessary to determine, for one, the moisture diffusion rates in the composite's principal axes so that moisture densities and distributions can be estimated for life-cycle exposures. In this study, moisture diffusion coefficients are determined for quasiisotropic Kevlar 49 181-style fabric reinforced Narmco 5208 epoxy laminates, and for the epoxy and fabric components individually. A microbalance technique is employed to continuously monitor the percentage weight gain of specimens exposed to 76 percent relative humidity at room temperature. The anisotropy of moisture diffusivity in the composite laminates is determined by use of a slope ratio (absorption vs time) technique and specimens of appropriate geometry. Results show that moisture diffuses in the laminate plane (6.6 x 10/sup -8/ cm/sup 2//sec) two orders of magnitude faster than through the thickness (1.9 x 10/sup -10/ cm/sup 2//sec). These values compare to a resin diffusivity of 7.1 x 10/sup -10/ cm/sup 2//sec. It is speculated that the rapid inplane diffusion is due to the preferential diffusion of moisture in the filament along its length.

• Research Organization: Sandia Labs., Albuquerque, NM (USA)
• DOE Contract Number: EY-76-C-04-0789
• OSTI ID: 6935563
• Report Number(s): SAND-78-0412C; CONF-780347-1
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
360404* -- Materials-- Polymers & Plastics-- Physical Properties-- (-1987)
ARAMIDS
DIFFUSION
EPOXIDES
FIBERS
FLUIDS
GASES
LAMELLAE
MATERIALS
ORGANIC COMPOUNDS
ORGANIC OXYGEN COMPOUNDS
PERMEABILITY
PETROCHEMICALS
PETROLEUM PRODUCTS
PLASTICS
REINFORCED MATERIALS
REINFORCED PLASTICS
VAPORS
WATER VAPOR