Anomalous solid-particle erosion rate of hot-pressed silicon carbide
Journal Article
·
· J. Am. Ceram. Soc.; (United States)
The steady-state erosion rate of a commercial hot-pressed SiC was investigated using angular Al/sub 2/O/sub 3/ particles. An anomalous size dependence was observed which may be due to grain boundries. (DLC)
- Research Organization:
- Argonne National Lab., IL
- DOE Contract Number:
- W-31-109-ENG-38
- OSTI ID:
- 6798878
- Journal Information:
- J. Am. Ceram. Soc.; (United States), Vol. 63:9/10
- Country of Publication:
- United States
- Language:
- English
Similar Records
Erosion of a silicon carbide whisker reinforced silicon nitride
Solid-particle erosion of in-situ reinforced Si[sub 3]Ni[sub 4]
Solid-particle erosion of in-situ reinforced Si{sub 3}Ni{sub 4}
Conference
·
Mon Dec 01 00:00:00 EST 1986
·
OSTI ID:6798878
Solid-particle erosion of in-situ reinforced Si[sub 3]Ni[sub 4]
Conference
·
Wed Apr 01 00:00:00 EST 1992
·
OSTI ID:6798878
+2 more
Solid-particle erosion of in-situ reinforced Si{sub 3}Ni{sub 4}
Conference
·
Wed Apr 01 00:00:00 EST 1992
·
OSTI ID:6798878
+2 more
Related Subjects
36 MATERIALS SCIENCE
SILICON CARBIDES
EROSION
ALUMINIUM OXIDES
GRAIN BOUNDARIES
HOT PRESSING
PARTICLES
ALUMINIUM COMPOUNDS
CARBIDES
CARBON COMPOUNDS
CHALCOGENIDES
CRYSTAL STRUCTURE
FABRICATION
MATERIALS WORKING
MICROSTRUCTURE
OXIDES
OXYGEN COMPOUNDS
PRESSING
SILICON COMPOUNDS
360205* - Ceramics
Cermets
& Refractories- Corrosion & Erosion
SILICON CARBIDES
EROSION
ALUMINIUM OXIDES
GRAIN BOUNDARIES
HOT PRESSING
PARTICLES
ALUMINIUM COMPOUNDS
CARBIDES
CARBON COMPOUNDS
CHALCOGENIDES
CRYSTAL STRUCTURE
FABRICATION
MATERIALS WORKING
MICROSTRUCTURE
OXIDES
OXYGEN COMPOUNDS
PRESSING
SILICON COMPOUNDS
360205* - Ceramics
Cermets
& Refractories- Corrosion & Erosion